利用无压、热压、放电等离子三种烧结方法制备了高密度、层片状的LaPO4陶瓷.测定、表征了三种烧结路线合成LaPO4陶瓷的致密化程度、织构行为及基本力学性能.同时,基于Al2O3和LaPO4相之间可形成弱结合界面,无压烧结制备了可用硬质合金钢钻头钻孔的40wt%Al2O3/LaPO4可加工复合材料.
参考文献
[1] | Marshall D B, Evans A G. J. Am. Ceranc. Soc., 1985, 68 (5): 225-231. |
[2] | Naslain R, Dugne O, Guette A. J. Am. Ceram. Soc., 1991, 74 (10): 2482-2488. |
[3] | Toyama N, Kishi T. J. Ceram. Soc. Jap., 2001, 109 (3): 244-247. |
[4] | Viricelle J P, Goursat P, Bahloul-Hourlier D. Composite Science and Technology, 2001, 61 (4): 607-614. |
[5] | Davis J B, Marshall D B, Morgan P E D. J. Eur. Ceram. Soc., 1999, 19: 2421-2426. |
[6] | Davis J B, Marshall D B, Housley R M, et al. J. Am. Ceram. Soc., 1998, 81 (8): 2169-2175. |
[7] | Wang Ruigang, Pan Wei. Ceramic International, 2002, 29 (1): 19-25. |
[8] | Ruh R, Donaldson K Y, Hasselman D P H. J. Am. Ceramc. Soc., 1992, 75 (10): 2887-2890. |
[9] | Xu H H H, Jahanmir S. J. Am. Ceramc. Soc., 1995, 78 (2): 497-500. |
[10] | Barsoum, Michel W. Scripta Materialia, 1997, 36 (5): 535-541. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%