凝胶注模成型技术由于使用了具有神经毒性的单体-丙烯酰胺在一定程度上限制了其在工业上的应用.本实验利用低毒的甲基丙烯酸羟乙酯凝胶注模成型Al2O3,研究了在该体系下低粘度高固相体积分数浓悬浮体的流变性及其固化过程.对比研究了JN281和柠檬酸铵两种分散剂对Al2O3浆料流变特性的影响,结果表明:对于该新体系JN281比常用的柠檬酸铵更有效.加入适量JN281可得到低粘度的高固相含量(≥50%)的陶瓷浆料.由新体系凝胶注模得到的素坯表面光滑,强度可达18MPa,SEM照片显示素坯具有均匀的显微结构,最终可烧结出均匀致密内部无明显缺陷的陶瓷部件.
参考文献
| [1] | Omatete O O, Janney M A, Strehlow R A. Am. Ceram. Soc. Bull., 1991, 70(10): 1641-1647. |
| [2] | Young A C, Omatete O O, Janney M A, et al. J. Am. Ceram. Soc., 1991, 74(3): 612-618. |
| [3] | Janney A M, Omatete O O. Method for molding ceramics powders using a water based gelcasting process. US patent, No. 5145908, Sept. 8, 1992. |
| [4] | Olhero S M, TariG, Coimbra M A, et al. J. Europ. Ceram. Soc., 2000, 20(4): 423-429. |
| [5] | Chen Y L, Xie Z P, Yang J L, et al. J. Europ. Ceram. Soc., 1999, 19(2): 271-275. |
| [6] | Xie Z P, Chen Y L, Huang Y. J. Europ. Ceram. Soc., 2000, 20 (3): 253-257. |
| [7] | Xie,etal.硅酸盐学报(Jounal ofthe Chinese Ceramic Society),1999,27(1):16-21. |
| [8] | Xie,et al.硅酸盐学报(Jounal ofthe Chinese Ceramic Society),1999,27(5):527-532. |
| [9] | Janney M A, Omatete O O, Walls C A, et al. J. Am. Ceram. Soc., 1998, 81(3): 581-591. |
| [10] | Barnes H A, Hutton J F, Walers K. An Introduction to Rheology, Oxford: Elsevier Press, 1989.128-131. |
| [11] | Hoffman R L. Trans. Soc. Rheol., 1972, 16: 155-173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%