开展了气流粉碎B4C粉末(比表面积2.53m2/g)的掺碳烧结实验,研究了掺碳剂种类、掺碳量、烧结温度、比表面积等对B4C烧结密度的影响.结果表明,掺碳显著促进B4C的烧结;在炭黑、葡萄糖和酚醛树酯三种掺碳剂中,掺入酚醛树酯可以获得最高的烧结密度;并且最佳的掺碳量为3%～5%C.B4C+3%C(酚醛树酯)分别经2200和2250℃烧结后的密度为92.1%TD和94.4%TD.若采用振动球磨B4C粉末(8.30m2/g)进行掺碳烧结实验,则可使2200℃的烧结密度提高到95.6%TD.
参考文献
| [1] | 王零森,蒋辉珍,杨菊美,等.中南矿冶学院学报,1985,16(4):66-72. |
| [2] | Prochazka S, Dole S L. Development of spacecraft materials and structure fundamentals. AD-A 161338, 1985. 29-39. |
| [3] | Schwetz K A, Vogt G. Process for the production of dense sintered shaped articles of polycrystalline boron carbide by pressureless sintering. US Pat 4195066, 1980-03-25. |
| [4] | Prochazka S, Grellner W. J. Less-Common Met., 1981, 82: 37-47. |
| [5] | 李朝端.原子能科学技术,2001,35(增刊):125-130. |
| [6] | 尹邦跃,王零森,边立刚,等.粉末冶金技术,2001,19(6):361-364. |
| [7] | 尹邦跃,王零森,方演初(YIN Bang-Yue,et al).硅酸盐学报(Journal of the Chinese Ceramic Society),2001,29(1):68-71. |
| [8] | 尹邦跃,王零森,方演初(YIN Bang-Yue,et al).无机材料学报(Journal of Inorganic Materials),2002,17(2):343-347. |
| [9] | Henney J W, Jones J W S. Sintered boron carbide containing free carbon. Brit. UK Pat 2014193,1979. |
| [10] | Thevenot F. J. Nucl. Mater., 1988, 152: 154-162. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%