以Ca(NO3)2.4H2O和(NH3)2HPO4为原料,用沉淀法合成羟基磷灰石(HA).在合成过程中添加明胶,考察明胶对HA成核、生长、粉末形态及热稳定性的影响.研究表明:当明胶加入量超过4wt%时,将阻碍HA的成核和生长;加4wt%明胶合成的粉末,经900℃煅烧,其平均颗粒尺寸为40nm,明显小于未加明胶的HA粉末,但热稳定性较差;在1000℃煅烧便有部分羟基磷灰石分解,生成β-磷酸钙.此β-磷酸钙煅烧至1500℃呈熔融态,仍没有相变为α-磷酸钙,具有很好的热稳定性.
参考文献
| [1] | Hong Y, Neil C, Ozin A G. Nature, 1994, 139 (17): 692-695. |
| [2] | Cha N J, Stucky D G, Mores E D, et al. Nature, 2000, 403 (20): 298-292. |
| [3] | Stephen M. Nature, 1993, 365 (7): 499-505. |
| [4] | Rhee S H, Tanaka J. Biomaterials, 1999, 20 (22): 2155-2160. |
| [5] | Brecevic L, Milhofer H D. Calcif Tissue Int., 1979, 2: 131-136. |
| [6] | Samuel I Stupp, Paul V. Nature, 1997, 277: 1243-1248. |
| [7] | Yin Y J, Zhao F, Yao K D, et al. J. App. Poly. Sci., 2000, 77 (18): 2929-2938. |
| [8] | Wen S L. Electron Microsc. Rev., 1989, 2: 1-16. |
| [9] | Petrov O E, Dyulgerova E, Petro L, et al. Mater. Lett., 2001, 48 (3-4): 162-167. |
| [10] | Wong A T C, Czemuszka J T. Colloids and Surfaces A: Physicochenical and Engineering Aspects,1993, 78(15): 245-251. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%