采用液相聚合相分离技术制备了多孔碳,并用压汞仪、BET比表面仪及扫描电镜对多孔碳性能进行表征.研究了制备工艺(热聚合制度和醇的种类)对多孔碳性能的影响.结果表明:热解后的多孔碳为无定形的碳,随着热聚合温度的升高,多孔碳粒子减小,平均孔径也减小,孔隙率增加,当采用40℃(3h)→100℃(24h)热聚合制度时,多孔碳的平均孔径为1.75μm,孔隙率为51.86%;选用不同的醇得到平均孔径在20.00～0.01μm之间变化,BET比表面积为350～400m2.g-1及孔径分布非常窄的多孔碳.
参考文献
| [1] | Schueller O J, Brittain S T, Whitesides G M. Sensors and Actuators A, 1999, 72: 125-139. |
| [2] | Takashi K. Carbon, 2000, 38: 269-286. |
| [3] | Hu Z H, Srinivasan M P. Carbon, 2001, 39: 877-886. |
| [4] | Lukaszewicz J P. Thin Solid Films, 2001, 391: 270-274. |
| [5] | Keith L H, Greg G H, David H S. Carbon, 2002, 40: 743-749. |
| [6] | Behrendt D R, Singh M. Journal of Materials Synthesis and Processing, 1994, 2(2): 117-123. |
| [7] | Singh M, Behrendt D R. J. Mater. Res., 1994, 9(7): 1701-1708. |
| [8] | Chiang Y T, Robert P. Mater. Sci. Eng A, 1991, 144: 63-74. |
| [9] | Hozer L, Lee R J, Chiang Y T. Mater. Sci. Eng. A, 1995, 195: 131-143. |
| [10] | Hozer L, Chiang Y T. J. Mater. Res., 1996, 11(9): 2346-2357. |
| [11] | Hashimoto T, Takenaka M, Jinnal H. Polym. Communi., 1989, 30: 177-179. |
| [12] | Schwahm D, Janen S, Müller G, Springer T, et al. Physica B, 1995, 213: 688-690. |
| [13] | Nose T. Phase Trans., 1987, 8: 245-260. |
| [14] | Tanaka H. Phys. Rev. Lett., 1996, 76(5): 187-190. |
| [15] | Tanaka H. Phys. Rev. Lett., 1993, 71(19): 3158-3161. |
| [16] | Constant K P, Lee J R, Ching Y M. J. Mater. Res., 1996, 11(9): 2338-2345. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%