采用聚乙二醇(PEG)先与钙反应后,再与磷源溶液反应,在低温环境中制得无定形磷酸钙.借助XRD分析讨论了PEG:CaCl2配比及PEG分子量与形成无定形磷酸钙之间的关系,实验结果表明,PEG:CaCl2配比为1:1和PEG分子量为10000是形成稳定无定形磷酸钙的最佳条件.其PEG稳定无定形磷酸钙的作用可理解为:在合成过程中PEG易存在于无定形磷酸钙Ca9(PO4)6团簇之间和吸附在无定形磷酸钙颗粒周围,有效地阻止了无定形磷酸钙向晶态的转变.
参考文献
[1] | Yohji I, Aya F, Mariko W. J. Biomat. Sci.: Polym. Ed., 1999, 10: 773-786. |
[2] | Linhart W, Peters F, Lehmann W, et al. J. Biomed. Mater. Res., 2001, 54: 162-171. |
[3] | Elliot J C. Studies in Inorganic Chemistry 18:Structure and Chemistry of the Apatites and Other calcium orthophosphates Elsevier, Inc., 1994. 53. |
[4] | Posner A S, Betts F. Accounts Chem. Res., 1975, 8: 273-281. |
[5] | Tadic D, Peters F, Epple M. Biomaterials, 2002, 23: 2553-2559. |
[6] | Skrtic D, Antonucci J M, Eanes E D, et al. J. Biomed. Mater. Res., 2002, 59: 597-604. |
[7] | Bertoni E, Bigi A, Falini G, et al. J. Mater. Chem., 1999, 9: 779-782. |
[8] | Liu Y, Wang W, Zhan Y, et al. Mater. Lett., 2002, 56: 496-501. |
[9] | 宋云京,李木森,温树林,等,电子显微学报,2002,21:695-696. |
[10] | Saujanya C, Radhakrishnan S. Polymer, 2001, 42: 6723-6731. |
[11] | Tropp J, Blumenthal N C, Waugh J S. J. Am. Chem. Soc., 1983, 105: 22-26. |
[12] | Abbona F, Baronnet A. J. Cryst. Growth, 1996, 165: 98-105. |
[13] | Uekawa N, Sukegawa T, Kakegawa K, et al. J. Am. Ceram. Soc., 2002, 85: 329-334. |
[14] | 刘少华,朱汉荣,生物医学工程学杂志,1990,7:329-332. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%