探讨了NiO掺杂量对PMS-PZ-PT三元系陶瓷的微观结构和电性能的影响.实验结果表明:随着掺杂量的增加,物相组成由四方相向三方相转变;NiO在PMS-PZ-PT材料中的固溶度比较小;当掺杂量为0.02wt%时,εr,d33,kp,Qm等都有所提高,从而能获得好的压电性能,能满足超声马达实际使用的要求.
参考文献
[1] | 郭晓波,陈海,孟中岩(GUO Xiao-Bo,et al).硅酸盐学报(Journal ofthe Chinese Ceramic Society),2002,30(1):125-127. |
[2] | Ueha S, Tomikawa Y, Kurosawa M. Ultrasonic Motors, Oxford, Clarendon Press, 1993. 4-5. |
[3] | Zheng H, Reaney I M, Lee W E, et al, J. Euro. Ceram. Soc, 2001, 21: 1371-1375. |
[4] | Guo Xiaobo, Chen Haiyan, Meng Zhonhyan. Key Engineering Materials, 2002, 224-226: 1112-1115. |
[5] | Li Longtu, Yao Yijin, Mu Zhenhan. Ferroelectrics, 1980, 28: 403-406. |
[6] | Nadoliisky M M, Vassileva T K, Vitkov P B, et al, Ferroelectrics, 1992, 129: 141. |
[7] | Gao Y, Chen Y H, Ryu J. Appl. Phys, 2001, 40 (2A): 687-693. |
[8] | Yoon Seok-Jin, Kang H W, Kucheiko S I, et al, J. Am. Ceram. Soc, 1998, 81 (9): 2473-2476. |
[9] | 朱兴文,孙振鹤,王鸿(ZHU Xing-Weng, et al).硅酸盐学报(Journal of the Chinese Ceramic Society), 1992, 20 (6): 532-536. |
[10] | Nathalie Texier, Christian Courtois, et al, J. Euro. Ceram. Soc, 2001, 21: 1499-1502. |
[11] | Pribosic I, Makovec D, Drofenik M. J. Euro. Ceram. Soc, 2001, 21: 1327-1331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%