对(Bi1/2Na1/2)TiO3-BaTiO3压电陶瓷在准同型相界处的组成掺入不同量的La3+,研究掺杂对于体系结构、压电与介电性能的影响.结果表明,掺杂使得体系的弛豫铁电体特征更为明显,相变的弥散程度增大,室温下的介电常数增大;当掺杂量低于1.5%时,材料的d33值增大,但同时介电损耗也相对于基体有所增加.当掺杂量达到3%以后,陶瓷的压电性能严重降低.
参考文献
| [1] | Smolenskii G A, Isupov V A, Agranovskaya A I, et al. Soy. Phys. Solid State (Engl. Transl.), 1961, 2 (11):2651-2654. |
| [2] | Sakata K, Takenaka T, Naitou Y. Ferroelectrics, 1992, 131: 219-226. |
| [3] | Sakata K, Masuda Y. Ferroelectrics, 1974, 5: 347-349. |
| [4] | Takenaka T, Sakata K. Ferroelectrics, 1989, 95: 153-156. |
| [5] | Aree Herabut, Ahmad Safari. J. Am. Ceram. Soc., 1997, 80 (11): 2954-2958. |
| [6] | Takenaka T, Sakata K, Toda K. Jpn. J. Appl. Phys., 1989, 28: 59-62. |
| [7] | Takenaka T, Maruyama K, Sakata K. Jpn. J. Appl. Phys. 1991, 30 (gB): 2236-2239. |
| [8] | Vakhrushev S B, Isupov V A, Kvyatkovsky B E , et al. Ferroelectrics, 1985, 63: 153-160. |
| [9] | Smolensky G A, Isupov V A. Dokl. Akad. Nank., USSR., 1954, 96: 53-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%