混合价态的锰氧化物Pr1-xCaxMnO3 薄膜是近年来国际上超导体以及巨磁电阻领域的研究热点之一.本文采用化学溶液沉积方法在Pt/Ti/SiO2/Si基底上制备出Pr1-xCaxMnO3薄膜, 降低了材料成本; 前驱体中不使用鳌和剂, 简化了工艺.采用XRD、FT-IR、SEM、AFM、EPMA以及俄歇探针仪等方法对所制备的薄膜进行了表征.结果表明, 实验中以较低的温度实现了PCMO钙钛矿结构的晶化; 薄膜平整光滑致密, 各组分分布均匀, C杂质含量处于很低的水平.
参考文献
| [1] | Tomioka Y, Asamitsu A, Kuwahara H, et al. Physical Review B, 1996, 53: 1689-1692. |
| [2] | Kiryukhin V, Casa D, Hill J P, et al. Nature, 1997, 386: 813-815. |
| [3] | Miyano K, Tanaka T, Tomioka Y, et al. Physical Review Letters, 1997, 78: 4257-4260. |
| [4] | Singh S K, Palmer S B, Paul D McK, et al. Appl. Phys. Lett., 1996, 69 (2): 263-265. |
| [5] | Barratt J, Lees M R, Balakrishnan G, et al. Appl. Phys. Lett., 1996, 68: 424-426. |
| [6] | Liu S Q, Wu N J, Ignatiev A. Appl. Phys. Lett., 2000, 76: 2749-2751. |
| [7] | Haghiri-Gosnet A M, Hervieu M, Simon Ch, et al. J. Appl. Phys., 2000, 88 (6): 3545-3551. |
| [8] | Saraf L V, Ogale S B, Chen Z, et al. Phys. Rev. B, 2000, 62 (18): 11961-11964. |
| [9] | Yanagisawa O, Izumi M, Huang K H, et al. J. Magn. Magn. Mater., 2000, 211: 133-138. |
| [10] | Annika Pohj, Gunnar Westin, Kiell Jansson. Chem. Mat., 2002, 14: 1981-1988. |
| [11] | Jirak Z, Hejtmanek J, Pollert E, et al. J. Appl. Phys., 1997, 81 (8): 5790-5792. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%