采用短时间一次阳极氧化法制备了纳米级孔氧化铝(AAO)模板, 有效地缩短了模板的制备时间, 获得的AAO模板孔洞排列有序程度虽有所下降, 但分布依然均匀.该模板有效地增加了表面积, 为金属沉积提供了均匀的纳米孔洞.采用电沉积法在AAO模板上沉积了颗粒尺寸一致且分布均匀的钴催化剂层后, 用CVD法在该模板上生长纳米碳管.经SEM和TEM观察, 所制得的纳米碳管密度高直径分布均匀, 具有单一的竹节状结构, 而且直径远小于孔径.试用了生长动力学来解释这种竹节状纳米碳管的形成原因.
参考文献
| [1] | Sumlo Iijima. Nature, 1991, 354: 56-58. |
| [2] | Dong S R, Tu J P, Zhang X B. Materials Science and Engineering, 2001, 33 (1-2): 83-87. |
| [3] | Thostenson E T, Ren Z F, Chou T W. Composites Science and Technology, 2001, 61 (13): 1899-1912. |
| [4] | Frackowiak E, Jurewicz K, Delpeux S, et al. Jounnal of Power Sources, 2001, 97-98: 822-825. |
| [5] | Minett A, Fraysse J, Gang G, et al. Current Applied Physics, 2002, 2 (1): 61-64. |
| [6] | Tsukagoshi K, Yoneya N, Uryu S, et al. Physica B, 2002, 323 (1-4): 107-114. |
| [7] | 沈曾民, 赵东林. 新型炭材料, 2001, 16 (1): 1-4. |
| [8] | Li W Z, Liang C H, Qiu J S, et al. carbon, 2002, 40 (5): 791-794. |
| [9] | Cao L, Chen H Z, Wang M, et al. J. Phys. Chem. B, 2002, 106: 8971-8975. |
| [10] | Kim J M, Choi W B, Lee N S, et al. Diamond and Related Materials, 2000, 9 (3-6): 1184-1189. |
| [11] | Saito Y, Uemura S. Carbon, 2000, (38): 169-182. |
| [12] | Ren Z F, Huang Z P, Xu J W, et al. Science, 1998, 282: 1105-1107. |
| [13] | Xu J M. Infrared Physics Technology, 2001, 42: 485-491. |
| [14] | Fan S S, Michael G C, et al. Science, 1999, 283: 512-514. |
| [15] | Li W Z, Xie S S, Qin L X, et al. Science, 1996, 274: 1701-1704. |
| [16] | Mintmire J W, White C T. Carbon, 1995, 33 (7): 893-902. |
| [17] | Li Y F, Qiu J S, Zhao Z B, et al. Chem. Phys. Lett., 2002, 366: 544-550. |
| [18] | Lee C J, Park J H. J. Phys. Chem. B, 2001, 105: 2365-2368. |
| [19] | 包建春, 王克宇, 张宁, 等. 无机化学学报, 2002, 18: 1097-1100. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%