采用溶胶-凝胶法,在58S生物玻璃的基础上,分别用0.5wt%的氧化镁和氧化锌取代氧化钙制备了含镁和含锌的生物玻璃.压制的试样分别在600、700和800℃煅烧以做强度测试,并分析了600和800℃煅烧后的物相组成.结果表明,三种试样煅烧至800℃仍为玻璃态,而镁锌的掺入大幅度提高了生物玻璃的强度,这主要是因为Mg-O和Zn-O具有比Ca-O高的键能.模拟体液浸泡试验表明,镁和锌降低了羟基磷灰石的早期成核速度,但并不影响其后期的生长.浸泡三天后所有样品表面都被羟基磷灰石覆盖,表明了样品具有良好的生物活性.
参考文献
| [1] | Hench L L, Splinter R J, Allen W C, et al. J. Biomed. Mater. Res. Symp., 1971, 2: 117-141. |
| [2] | Zhong J P, Greenspan D C. J. Biomed. Mater. Res (Appl. Biomater.). 2000, 53: 694-701. |
| [3] | Laczka M, Cholewa-Kowalska K, Laczka-Osyczka A, et al. J. Biomed. Mater. Res., 2000, 52: 601-612. |
| [4] | Perez-Pariente J, Balans F, Vallet-R.egi M. Chem. Mater., 2000, 12: 750-755. |
| [5] | Perez-Pariente J, Balans F, Roman J, et al. J. Biomed. Mater. Res., 1999, 47: 170-175. |
| [6] | Underwood E J. Trace element in human and animal nutrition, 4th edition. London: Academic Press, 1997.196. |
| [7] | Hamilton E I, Minski M J, Cleary J J. Sci Total Environ 1972/73, 1: 341-374. |
| [8] | WHO Expert Committee on Trace Elements in Human Nutrition. Trace elements in human nutrition, WHO Tech Rep Ser, 1973, 532: 9-15. |
| [9] | Bettger W J, O' Dell B L. J. Nutr. Biochem., 1993, 4: 194-207. |
| [10] | Yamaguchi M, Yamaguchi R, Suketa Y. Biochem Pharmacol., 1986, 35: 773-777. |
| [11] | Kishi S, Yamaguchi M. Biochem. Pharmacol., 1994, 48: 1225-1230. |
| [12] | Moonga B S, Dempster Q W. J. Bone Miner. Res., 1995, 10: 453-457. |
| [13] | Kokubo T, Kushitani H, Sakka S, et al. J. Biomed. Mater. Res., 1990, 24: 721. |
| [14] | Balas F, Perez-Pariente J, Vallet-Regi M. Bioceramica., 1998, 11: 125-128.. |
| [15] | Oliveia J M, Correia R N, Fernandes M H. Biomaterials, 2002, 23: 371-379. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%