以乙二胺为前驱液,采用高温热解法,860.C下在镍基底表面生长CNx纳米管薄膜.研究了经过不同实验条件处理过的镍基底表面的CNx纳米管的生长情况.实验结果表明,经过不同的预处理过程后,镍基底对CNx纳米管的生长表现出不同的催化性能,经过氢氟酸(HF)浸泡10min并无水乙醇超声清洗过的镍基底有利于具有"竹节状"结构的CNx纳米管的生长.
参考文献
[1] | Fan S S, Chapling M G, Franklin N R, et al. Science, 1999, 283: 512-514. |
[2] | Pan Z W, Au F C K, Lai H L, et al. J. Phys. Chem. B, 2001, 105(8): 1519-1522. |
[3] | Yoon Y J, Baik H K. J. Vac. Sci. Tech. B, 2001, 19(1): 27-31. |
[4] | Schlittler R R, Seo J W, Gimzewski J K, et al. Science, 2001, 292: 1136-1139. |
[5] | Bonard J M, Croci M, Klinke C, et al. Carbon, 2002, 40(10): 1715-1728. |
[6] | Suh J S, Jeong K S, Lee J S, et al. Appl. Phys. Lett., 2002, 80(13): 2392-2394. |
[7] | Baughman R H, Zakhidov A A, de Heer W A. Science, 2002, 297: 787-792. |
[8] | Kaatz F H, Siegal M P, Overmyer D L, et al. Mater. Sci. Engineeing C, 2003, 23: 141-144. |
[9] | Sen Rahul, Satishkumar B C, Govindaraj A, et al. Chem. Phys. Lett., 1998, 287: 671-676. |
[10] | Terrones M, Terrones H, Grobert N, et al. Appl. Phys. Lett., 1999, 75(25): 3932-3935. |
[11] | Terrones M, Redlich P, Grobert N, et al. Adv. Mater., 1999, 11(8): 655-658. |
[12] | Han W Q, Kohler-Redlich P, Seeger T, et al. Appl. Phys. Lett., 2000, 77(12): 1807-1809. |
[13] | Satishkumar B C, Govindaraj A, Harikumar K R, et al. Chem. Phys. Lett., 1999, 300: 473-477. |
[14] | Han W Q, Bardo Y, Kurashima K, et al. Appl. Phys. Lett., 1998, 73(21): 3085-3088. |
[15] | Bai X D, Guo J D, Yu J, et al. Appl. Phys. Lett., 2000, 76(18): 2624-2626. |
[16] | Terrones M, Benito A M, Manteca-Diego C, et al. Chem. Phys. Lett., 1996, 257: 576-582. |
[17] | 张红瑞,梁二军,丁佩,等.物理学报,2002,51(12):2901-2905. |
[18] | Migamoto Y , Cohen M L , Louie S G. Solid State Commun., 1997, 102(8): 605-608. |
[19] | Hernandez E , Goze C, Bernier P, et al. Appl. Phys. A: Mater. Sci.. Process., 1999, 68(3): 287-292 |
[20] | Ma X C, Wang E G, Zhou W Z , et al. Appl. Phys. Lett., 1999, 75(20): 3105-3107. |
[21] | Zhong D Y, Liu S, Zhang G Y, et al. J. Appl. Phys., 2001, 89(11): 5939-5943. |
[22] | Zhang G Y, Ma X C, Zhong D Y, et al. J. Appl. Phys., 2002, 91(11): 9324-9332. |
[23] | Golberg D, Dorozhkin P S, Bando Y, et al. Appl. Phys. A, 2003, 76: 499-507. |
[24] | Wang X B, Liu Y Q, Zhu D B, et al. J. Phys. Chem. B, 2002, 106: 2186-2190. |
[25] | Chen Y, Deng S Z, Xu N S, et al. Mater. Sci. Engineeing A, 2002, 327(1): 16-20. |
[26] | 丁佩,晁明举,梁二军,等.物理学报,2004,53(8):2786-2791. |
[27] | 丁佩,梁二军,张红瑞,等.物理学报,2003,52(1):237-241. |
[28] | Liang E J, Ding P, Zhang H R, et al. Diamond and Related Materials, 2004, 13(1): 69-73. |
[29] | 丁佩,梁二军,张红瑞,等.物理学报,2004,53(5):1546-1551. |
[30] | 梁二军,张红瑞,刘一真,等.光散射学报,2001,13:205-209. |
[31] | Terrones M, Ajayan P M, Banhart F, et al. Appl. Phys. A, 2002, 74: 355-361. |
[32] | Endo M, Kim Y A, Fukai Y, et al. Appl. Phys. Lett., 2001, 79(10): 1531-1533. |
[33] | Kanzow H, Lenski C, Ding A. Phys. Rev. B, 2001, 63(12): 125402-125408. |
[34] | Kukovitsky E F, Lvov S G, Sainov N A, et al. Chem. Phys. Lett., 2002, 355: 497-503. |
[35] | Wen Y K, Shen Z M . Carbon, 2001, 39(15): 2369-2374. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%