采用溶析结晶法制备亚微米硫酸钡粒子,并运用TEM、SEM、XRD、激光粒度分析仪等分析方法对粒子的粒径、粒度分布、形貌和晶相进行了表征.结果表明溶析结晶法制备的粒子平均粒径160～750nm、粒度分布均匀、纯度高、晶相完整.考察了结晶温度、加料方式、搅拌速率和料液浓度等过程参数以及分散剂对硫酸钡粒子的影响,发现较低的结晶温度、反向加料方式、较快的搅拌速率、一定的料液浓度等因素有利于制备亚微米硫酸钡粒子.
参考文献
| [1] | Mineral Commodity Summaries, U.S. Geological Survey, January 2004. |
| [2] | 顾薇娜.中国非金属矿工业导刊,1998,5(5):38-39. |
| [3] | 矿产资源综合利用手册,科学出版社,2000.521. |
| [4] | Wang K, Wu J S, Zeng H M. European Polymer Journal, 2003, 39: 1647-1652. |
| [5] | Boden D P. Journal of Power Sources, 1998, 73: 89-92. |
| [6] | Chen G G, Luo G S, Xu J H, et al. Powder Technology, 2004, 139: 180-185. |
| [7] | Ginebra M P, Aparicio C, Albuixech L, et al. Journal of Materials Science: Materials in Medicine, 1999, 10:733-737. |
| [8] | Ivanova N I, Rudelev D S, Summ B D, et al. Colloid Journal, 2001, 63(6): 714-717. |
| [9] | Take E, Yekeler M, Ulusoy U, et al. International Journal of Mineral Processing, 2002, 67: 29-42. |
| [10] | Jones F, Oliveira A, Rohl A L, et al. Journal of Crystal Growth, 2002, 237-239: 424-429. |
| [11] | Uchida M, Sue A, Yoshioka T, et al. Journal of Materials Science Letters, 2000, 19: 1373-1374. |
| [12] | Hopwood J D, Mann S. Chemistry of Materials, 1997, 9: 1819-1828. |
| [13] | Archibald D D, Gaber B P, Hopwood J D, et al. Journal of Crystal Growth, 1997, 172: 231-248. |
| [14] | Alfassi Z B, Mosseri S. AICHE Journal, 1984, 30(5): 874-876. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%