在线测量了自制含锶羟基磷灰石骨水泥(Sr-CPC)浆体在水化过程中的pH值实时变化以及各固化体在培养液中浸泡不同时间后其浸提液的pH值,并利用MTT比色法评价了该水泥固化体的体外细胞毒性.XRD与FTIR分析表明,固化体在SBF中浸泡24h后,水化产物为锶钙羟基磷灰石固溶体,而且该固溶体中含有与骨磷灰石类似的CO23-;各水泥浆体pH值的在线测量表明,不同含锶量水泥浆体的pH基本在6.5～7.8之间变化,接近中性;体外细胞毒性试验表明,不同含锶量水泥固化体的细胞毒性为0或1级,且细胞毒性与各水泥固化体浸提液的浓度、作用时间有一定的关联性.
参考文献
| [1] | Quanzu Y, Tom T, Dean-mo Liu. Biomater., 2002, 23: 2751-2760. |
| [2] | Santos C, Luklinska Z B, Clarke R L, et al. M. J. Mater. Sci. Mater. Med., 2001, 12 (7): 565-573. |
| [3] | Markovic M, Takagi S, Kim D, et al. J. Dent. Res., 1997, 76: 2942. |
| [4] | Liu C S, Shao H F, Chen F C, et al. Biomater., 2003, 24: 4103-4113. |
| [5] | Friedman C D, Constantino P D, Jones K, et al. Otolaryngol. Head. Neck. Surg., 1991, 117: 385-389. |
| [6] | Christoffersen J, Christoffersen M R, Kolthoff N, et al. Bone., 1997, 20: 47-54. |
| [7] | Chen D M, Fu Y F, Gu G Z, et al. Chin. J. Biomed. Eng., 2003, 20: 278-280. |
| [8] | Grynpa M D, Hamilton E, Cheung R, et al. Bone, 1996, 18: 253-259. |
| [9] | Johal K K, Mendoza-Suarez G, Brook J I. J. Mater. Sci. Mater. Med., 2002, 13 (4): 375-379. |
| [10] | 廖大鹏,周正炎,顾云峰,等(LIAO Da-Peng,et al).口腔颌面外科杂志(J.Stomatol.Maxil.Sug.).2001,11(2):122-126. |
| [11] | Lerous L, Lacout J L. J. Mater. Res., 2001, 16: 171-178. |
| [12] | 郭大刚,付涛,徐可为(GUO Da-Gang,et al).硅酸盐学报(J.Chin.Cerm.Soc.).2002,30(2):189-192. |
| [13] | Contanz B, Ison I C, Fulmer M T, et al. Science, 1995, 267:1796 |
| [14] | 刘昌胜(Liu Chang-sheng,et al).博士论文(Doctorial Dissertation).华东理工大学,1996.10. |
| [15] | 司徒镇强,吴军正,刘斌,等(SI-TU Zhen-Qiang,et al).细胞培养(Cell Culture),世界图书出版公司(第一版).1996. |
| [16] | Shorr E, Carter A C. Bull. Hosp. Jt. Dis. Orthop. Inst., 1952, 13: 59-66. |
| [17] | 孙浩亮,郭大刚,徐可为,等(SUN Hao-Liang,et al).硅酸盐学报(J.Chin.Cerm.Soc.),(已录用). |
| [18] | 陈德敏,傅远飞(CHEN De-Min,et al).现代口腔医学杂志(J.Modern.Stomato1.),2003,17(6):501-503. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%