以自制的NaHSe乙醇溶液为硒源,在PEG-400无水体系中采用多元醇法,在180℃生长10h制备了直径100～200nm,长度可达十几微米的纳米线.产物通过XRD、TEM、HRTEM、FESEM、EDS和UV-Vis等手段进行了表征,并研究了不同多元醇对产物形貌的影响.研究表明,PEG-400作为结构导向剂在制备一维Sb2Se3纳米线中发挥着至关重要的作用,并且无水环境为纳米晶的生长提供了更加纯净的条件,有利于制备高质量的纳米晶.
参考文献
| [1] | Fernández A M, Merino M G. Thin Solid Films, 2000, 366: 202-206. |
| [2] | Wang D, Yu D, Shao M, et al. Mater. Chem. Phys., 2003, 82: 546-550. |
| [3] | Xie Q, Liu Z, Shao M, et al. J. Crystal Growth, 2003, 252: 570-574. |
| [4] | Zheng X, Xie Y, Zhu L, et al. Inorg. Chem., 2002, 41: 455-461. |
| [5] | 王为,张伟玲,王惠,等(WANG Wei,et al).无机材料学报(Joumal of Inorganic Materials),2004,19(1):127-132. |
| [6] | Xia Y, Yang P, Sun Y, et al. Adv. Mater., 2003, 15: 353-389. |
| [7] | Sun Y, Xia Y. Science, 2002, 298: 2176-2179. |
| [8] | Sun Y, Xia Y. Adv. Mater., 2002, 14: 833-837. |
| [9] | Sun Y, Mayers B, Herricks T, et al. Nano Lett., 2003, 7: 955-960. |
| [10] | Ma X, Zhang Z, Wang X, et al. J. Crystal Growth, 2004, 263: 491-497. |
| [11] | Wang D, Yu D, Mo M, et al. J. Crystal Growth, 2003, 253: 445-451. |
| [12] | Shen G, Chen D, Tang K, et al. J. Crystal Growth, 2003, 252: 350-354. |
| [13] | Klayman D L, Griffin T S. J. Am. Chem. Soc., 1973, 95: 197-199. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%