用溶胶-凝胶法制得复合半导体WO3-TiO2,用浸渍法制得Cu/WO3-TiO2光催化剂.利用XRD、Raman、TPR、IR、TEM、XPS和UV-Vis等技术研究了Cu/WO3-TiO2的物相结构、微粒尺寸和吸光性能.结果表明:含量为10wt%的WO3单分子层分散在TiO2表面,粉体平均粒径15nm.WO3的引入使TiO2吸收限发生明显蓝移,WO3负载量超过单分子层分散(＞10wt%),有晶相WO3生成,光吸收性能下降.W-O-Ti键的形成加强了半导体之间的相互作用,有利于光生载流子在半导体间的输送.负载金属Cu促进四面体配位W向八面体配位W转化.
参考文献
| [1] | Tryk D A, Fujishima A, Honda K. Electrochimica. Acta., 2000, 45 (15/16): 2363-2376. |
| [2] | Linsebigler A L, Lu G, Yates J T Jr. Chem. Rev., 1995, 95 (3): 735-758. |
| [3] | 姜洪波,高濂,张青红(JIANG Hong-Bo,et al).无机材料学报(Journal ofInorganic Materials),2003,18(3):695-699. |
| [4] | Gouvêa C A K, Wypych F, Moraes S G. Chemosphere., 2000, 40 (4): 427-432. |
| [5] | Young T K, Kang Y S, Wan I L. J. Catal., 2000, 191 (1): 192-199. |
| [6] | 柳清菊,杨喜昆,刘强(LIU Qing-Ju,et al).无机材料学报(Journal ofInorganic Materials),2004,19(1):140-146. |
| [7] | Bates C W Jr. Materials. Letters., 1995, 23 (1-3): 1-5. |
| [8] | Yang J J, Li D X, Zhang Zh J, et al. J. Photochemistry and Photobiology A., 2000, 137 (2/3): 197-202. |
| [9] | Vermaire D C, Berge P C. J. Catal., 1989, 116 (2): 309-317. |
| [10] | 陈崧哲,钟顺和(CHEN Song-Zhe,et al).应用化学(Chin Appl Chem),2003,20(1):23-28. |
| [11] | Benitez V M, Querini C A, Figoli N S. Appl. Catal., 2003, 252 (2): 427-436. |
| [12] | Huang Y Y, Zhao B Y, Xie Y C. Appl. Catal., 1998, 171 (1): 75-83. |
| [13] | Moulder J F, Stickle W F, Spbol P E, et al. Handbook of X-Ray Photoeletron Spectroscopy, USA: Perkin-Elmer Corp, 1992. 220. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%