采用射频磁控溅射制备了FePt(50nm)和[FePt(2,3,5nm)/AlN(1nm)]n膜,之后在550℃退火30min,研究了周期数(n)和AlN含量对[FePt/AlN]n系列多层膜结构及磁性的影响.结果表明,多层膜的矫顽力和矩形比均在n=8时出现较大值;周期数的增大会引起晶粒尺寸的长大;AlN的加入不但可以抑制FePt粒子的长大,使晶粒体积(Vgrain)和磁激活体积(V*)趋于一致,而且还能有效地降低晶粒间交换耦合作用,并且AlN含量越大,晶粒间交换耦合作用的程度越弱.
参考文献
| [1] | Chen S C, Kuo P C, Lie C T, et al. J. Magn. Magn. Mater., 2001, 236: 151-157. |
| [2] | Bian B, Laughlin D E, Sato K, et al. J. Appl. Phys., 2000, 87(9): 6962-6964. |
| [3] | Zhang Y, Wan J, Bonder M J, et al. J. Appl. Phys., 2003, 93(10): 7175-7177. |
| [4] | 杨涛,于广华,黄阀,等.科学通报,2002,47(23):1778-1780. |
| [5] | Bai J, Yang Z, Wei F, et al. J. Magn. Magn. Mater., 2003, 257: 132-137. |
| [6] | Yah M L, Zeng H, Powers N, et al. J. Appl. Phys., 2002, 91(10): 8471-8473. |
| [7] | Luo C P, Liou S H, Sellmyer D J. J. Appl. Phys., 2000, 87(9): 6941-6943. |
| [8] | Daniil M, Farber P A, Okumura H, et al. J. Magn. Magn. Mater., 2002, 246: 297-302. |
| [9] | Xu Xiao-Hong, Wu Hai-Shun, Li Xiao-Li, et al. Physica B, 2004, 348: 436-439. |
| [10] | Wan J, Stoyanov S, Huang Y, et al. J. Magn. Magn. Mater., 2004,272-276: 1625-1627. |
| [11] | 许小红,张富强,武海顺,等(XU Xiao-Hong,et al).无机材料学报(Journal ofInorganic Materials),2001,16(6):1161-1168. |
| [12] | 许小红,武海顺,马文瑾,等(XU Xiao-Hong,et al).无机材料学报(Journal ofInorganic Materials),2003,18(2): 490-494. |
| [13] | Xu Xiao-Hong, Wu Hai-Shun, Wang Fang, et al. Appl. Surf. Sci., 2004, 233: 1. |
| [14] | Sellmyer D J, Luo C P, Yan M L, et al. IEEE Trans. Magn., 2001, 37: 1286. |
| [15] | Shimatsu T, Lodder J C, Sugita Y, et al. IEEE Trans. Magn., 1999, 35: 2697. |
| [16] | Huang Y, Okumura H, Hadjipanayis G C, et al. J. Magn. Magn. Mater., 2002, 242-245: 317-320. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%