研制的纳米孔玻态炭电极,整体呈纳米开孔结构,电容特性优良,全面超过了中孔碳气凝胶.其成孔机理研究表明:通过添加适量的固化剂一六次甲基四胺,经球磨固混后,调节固化温度,造成固化树脂颗粒内芯与外壳的交联度不同,形成"壳芯"结构;粉碎压制时,内芯作为外壳的粘合剂使材料成型,炭化时壳层不融化而阻挡内芯熔并成玻态炭.于是,碳粒内外形成丰富的开放孔隙,活化剂气体能够扩散渗入体相进行活化而得纳米孔玻态炭.
参考文献
| [1] | Nishino A.J Power Sources,1996,60:137-138. |
| [2] | Louis P J,Terrill B A,Peter J C.Journal of Power Sources,1999,79:60-63. |
| [3] | Hiroyuki N,Atsushi S,Kouichi M.J.Electrochem.Soc.,2000,147 (1):38-42. |
| [4] | Stanislaw B,Bozena D,Janusz S.Carbon,1995,33 (9):1255-1263. |
| [5] | Fitzer E,Schaefer W,Yamada S.Carbon,1969,7:643-648. |
| [6] | Braun A,Bartsch M.Materials.Research Society Symposium Proceedings,Warrendale,2000,575:369-380. |
| [7] | Braun A,Bartsch M.J of Non-crystalline Solids,1999,260:1-14. |
| [8] | 文越华,程杰,曹高萍,等.电源技术,2003,27(5):455-459. |
| [9] | Jenkins G M,Kawamura K.Polymer Carbon-Carbon Fiber,Glass and Char.England:Cambridge University Press,1976.37-75. |
| [10] | 文越华.北京防化研究院博士论文,2004.55-58. |
| [11] | 文越华,曹高萍.碳素,2002,2:32-36. |
| [12] | Koresh J,Soffer A.J.Electrochem.Soc.,1977,124 (9):1379-1384. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%