用常压烧结和热压烧结法分别制备了多晶Ca1+xB6(x=-0.02、0、0.02)陶瓷样品并对其铁磁性能进行系统分析.结果表明,在烧结温度低于1500℃范围内,不论样品富Ca或赤Ca,所有的样品均呈现铁磁性能;另外,两种方法制备的陶瓷样品虽然气孔率明显不同,而其铁磁性能并没有显著差异,认为CaB6样品存在的铁磁性机制不决定于样品中的Ca空位浓度和气孔率.
参考文献
[1] | Young D P,Hall D,Torelli M E,et al.Nature,1999,397(4):412-414. |
[2] | Souma S,Komatsu H,Takahashi T,et al.Physical Review Letters,2003 90 (2):027202. |
[3] | Murakami S,Shindou R,Nagaosa N,Mishchenko A S.Physical Review B,2002,66 (18):184405. |
[4] | Ceperley D.Nature,1999,397(4):386-387. |
[5] | Zhitomirsky M E,Rice T M,Anisimov V I.Nature,1999,402(18):251-252. |
[6] | Lofland S E,Seaman B,Ramanujachary K V,et al.Physical Review B,2003,67 (2):020410. |
[7] | Gianno K,Sologubenko A V,Ott H R,et al.Journal of Physics-Condensed Matter,2002 14 (5):1035-1043. |
[8] | Moriwaka T,Nishioka T,Sato N K.Journal of the Physical Society of Japan,2001,70(2):341-343. |
[9] | Monnier R,Delley B.Physical Review Letters,2002,87(15):157204. |
[10] | Vonlanthen P,Felder E,Degiorgi L,et al.Physical Review B,2001,62(15):10076. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%