采用含有过硫酸钾氧化剂和氢氧化钾的水溶液处理金属铜表面,再经空气中加热后,在铜表面上得到了一层具有花朵状纳米结构的CuO膜.每朵纳米花由数十个长约2μm、宽约120nm、厚约12nm的CuO纳米片自组装而成.纳米花膜经氟化处理后表现出超疏水性,接触角达到约158°.文中初步提出了纳米花形态的生长机制,并用Cassie理论对膜的润湿性进行了分析.
参考文献
| [1] | Barthlott W,Neinhuis C.Planta,1997,202 (1):1-8. |
| [2] | Onda T,Shibuichi S,Satoh N,et al.Langmuir,1996,12 (9):2125-2127. |
| [3] | Gao X F,Jiang L.Nature,2004,432:36. |
| [4] | Erbil H Y,Demircl A L,Avci Y,et al.Science,2003,299:1377-1380. |
| [5] | Richard D,Clanet C,QuéréD.Nature,2002,417:811. |
| [6] | Callies M,QuéréD.Soft Matter,2005,1 (1):55-61. |
| [7] | 江雷.科技导报,2005,23(2):4-8. |
| [8] | Nakajima A,Hashimoto K,Watanabe T.Monatsh.Chem.,2001,132:31-41. |
| [9] | Hou H,Xie Y,Li Q.Cryst.Growth Des.,2005,5 (1):201-206. |
| [10] | Zhang W,Wen X,Yang S,et al.Adv.Mater.,2003,15 (10):822-825. |
| [11] | Zhang W,Wen X,Yang S.Inorg.Chem.,2003,42 (16):5005-5014. |
| [12] | Yu H,Zhang Z,Han M,et al.J.Am.Chem.Soc.,2005,127:2378-2379. |
| [13] | Zhang Z,Yu H,Shao X,et al.Chem.Eur.J.,2005,11:3149-3154. |
| [14] | Wu J M,Hayakawa S,Tsuru K,et al.Scripta Mater.,2002,46:101-106. |
| [15] | Wu J M.J.Cryst.Growth,2004,269:347-355. |
| [16] | Vayssieres L.Int.J.Nanotechnology,2004,1 (1/2):1-41. |
| [17] | Cassie A,Baxter S.Trans.Faraday Soc.,1944,40:546-551. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%