利用中间相沥青纤维中沥青分子的高度择优取向和适度的热塑性热压制备高导热块体炭材料.对比研究了经不同氧化处理的带形及圆形中间相沥青纤维热压所得炭材料的传导性及力学性能.结果表明:相对圆形纤维来说,由于带形中间相纤维具有更高的纤维轴向取向度和纤维之间更高的接触面积,故其热压所得材料具有更高的密度和传导性.经260℃氧化的带形纤维热压所得炭材料的密度、抗弯强度、电阻率及热导率分别达到了2.18g/cm-3、118.4MPa、1.13μΩm和717W/m·K.
参考文献
| [1] | 孙乐民,李贺军,张守阳(SUN Le-Min,et al).无机材料学报(Journal of Inorganic Materials),2000,15(6):1111-1116. |
| [2] | Fitzer E.Carbon,1987,25 (2):163-190. |
| [3] | Hugh O.Pieson.Handbook of carbon,graphite,diamond and fullenenesroperties,processing and application.USA.Noyes Publication,1993.51-63. |
| [4] | Blazewicz S,Blocki J,Chlopek J,et al.Carbon,1996,34 (11):1393-1399. |
| [5] | 邱海鹏,郭全贵.宇航材料工艺,2001,31(6):23-26. |
| [6] | Adams P M,Katzman H A,Rellick G S,et al.Carbon,1998,36 (3):233-245. |
| [7] | 邱海鹏,宋永忠,郭全贵,等.功能材料,2002,33(5):473-476. |
| [8] | Barr J B,Hecht D H,Levan C D.High thermal conductivity panels from mesophase pitch fibers.Extended abstracts,22nd biennial Conf,on carbon.UC San Deigo (California.USA):American Carbon Society,1995.32-33. |
| [9] | Edie D D,Fain C C,Robinson K E,et al.Carbon,1993,31 (6):941-949. |
| [10] | Edie D D,Robinson K E,Fleurot O,et al.Carbon,1994,32 (6):1045-1054. |
| [11] | Gallego N C,Edie D D,Nysten B,et al.Carbon,2000,38 (7):1003-1010. |
| [12] | Callego N C,Edie D D.Composites:Part A 2001,32 (8):1038-1043. |
| [13] | 李安邦.新型炭材料,1999,14(1):80. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%