以KMnO4和N4(CH2)6为主要原料,在130℃反应16h,水热法制备了MnOOH纳米棒,并利用X射线粉末衍射(XRD)、透射电子显微镜(TEM)和高分辨透射电子显微镜(HRTEM)等手段对产物进行了表征.探索了KMnO4和N4(CH2)6间的摩尔比以及反应温度对合成产物的影响.实验结果表明:产物为具有单斜结构的MnOOH纯相,形貌为棒状,呈现单晶特性.
参考文献
| [1] | Kovtyukhova N I,Mallouk T E.Chem.Eur.J.,2002,8:4355-4359. |
| [2] | Han W Q,Fan S S,Li Q Q,et al.Science,1997,277:1287-1290. |
| [3] | Martin R.Science,1994,266:1961-1963. |
| [4] | Pacholski C,Kornowski A,Weller H.Angew.Chem.,2002,114:1234-1239. |
| [5] | Yang J,Xue C,Yu S H,et al.Angew.Chem.,2002,114:4891-4896. |
| [6] | Bach S,Henry M,Baffier N,et al.J.Solid State Chem.,1990,88:325-329. |
| [7] | Bach S,Pereira-Ramos J P,Baffier N,et al.Electrochim.Acta,1991,36:1595-1599. |
| [8] | Hunter J.J.Solid State Chem.,1981,39:142-145. |
| [9] | Bach S,Pereira-Ramos J P,Baffier N.J.Solid State Chem.,1995,120:70-76. |
| [10] | Al-Sagheer F A,Zaki,M I.Colloid Surface,2000,A 173:193-197. |
| [11] | Cordoba de Torresi S I,Gorenstein A.Electrochim.Acta,1992,37:2015-2018. |
| [12] | Kanasaku T,Amezawa K,Yamamoto N.Solid State Ionics,2000,133:51-56. |
| [13] | Brock S L,Duan N,Rong T Z,et al.Chem.Mater.,1998,10:2619-2623. |
| [14] | Wang X,Li Y D.Chem.Commun.,2002.764-766. |
| [15] | Wang X,Li Y D.J.Am.Chem.Soc.,2002,124:2881-2885. |
| [16] | Xiong Y J,Xie Y.Chem.Eur.J.2003,9:1645-1648. |
| [17] | Wang W Z,Xu C K,Wang G H,et al.Adv.Mater.,2002,14:837-843. |
| [18] | 张治安,杨邦朝,邓梅根,等(ZHANG Zhi-An,et al).无机材料学报(Journal of Inorganic Materials),2005,20(3):529-536. |
| [19] | Shamma P K,Whittingham M S.Mater.Lett.,2001,48:319-313. |
| [20] | Ocana M.Colloid Polyn.Sci.,2000,278:443-447. |
| [21] | 朱归胜,徐华蕊,廖春图,等(ZHU Gui-Sheng,et al).无机材料学报(Journal of Inorganic Materials),2005,20(2):479-483. |
| [22] | Zhang Y G,Liu Y,Guo F,et al.Solid State Commun.,2005,134:523-527. |
| [23] | 董喜燕,张兴堂,程纲,等(Dong Xi-Yian,et al).化学学报(Acta Chimica Sinica),2004,62:2441-2443. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%