采用低温燃烧法合成出掺钕钇铝石榴石(Nd:YAG)粉末,经模压300MPa成型,于1700℃真空烧结5h,制备出尺寸φ9mm×1mmNd:YAG透明陶瓷片.对Nd:YAG透明陶瓷片进行光透过率、场发射-环境扫描电镜测量.采用体视学原理与方法定量地研究了Nd:YAG透明陶瓷的微观结构参数和光透过率之间的关系.研究结果表明:尺寸φ9mm×1mmNd:YAG透明陶瓷片在可见光波段光透过率约为45%,在近红外光波段约为55%;随着入射光波长的增加,光透过率增加;随着晶粒三维球当径(D3S)的增加,光透过率增加,当D3S约为20pm时,Nd:YAG透明陶瓷光透过率接近单晶理论值;随着晶粒以及单个晶粒平均比表面积的增加,光透过率降低;随着晶粒三维平均自由距离的增加,光透过率降低.
参考文献
[1] | Jianren L U,Junhua LU.Advanced Solid-State Lasers,2002,68(1):507-517. |
[2] | 黄朝红,王爱华,殷绍唐,等.硅酸盐学报,2003,31(9):873-877. |
[3] | 闻雷,孙旭东,马伟民,等(WEN Lei,et al).无机材料学报(Journal of Inorganic Materials),2004,19(2):295-301. |
[4] | Ikesue Akio,Furusato Iso,Kamata Kiichiro.Journal of the American Ceramic Society,1995,78(1):225-228. |
[5] | Hay R S.Journal of the Materials Research,1993,8(3):578-604. |
[6] | Nyman May,Caruso James,Hampden Mark J.Journal of the American Ceramic Society,1997,80(5):1231-1 238. |
[7] | Sordelet D J,Akinc M,Panchula M L,et al.Journal of the European Ceramic Society,1994,14(1):123-130. |
[8] | 李江,潘裕柏,张俊计,等.硅酸盐学报,2004,31(5):490-493. |
[9] | Pechini M P.Method of preparing lead and alkaline earth titanate and niobates and coating method using the same to form a capacitor.US,330697,1967.7. |
[10] | ZHANG Huashan,SU Chunhui,HAN Hui,et al.Rare.Metals.,2005,24(2):166-1690. |
[11] | ZHANG Huashan,SU Chunhui,HAN Hui,et al.Journal of Rare.Earths,2005,23(3):304-308. |
[12] | Vaqueiro Paz,López-Quintela M Arturo.Journal of Materials Chemistry,1998,8(1):161-163. |
[13] | 刘国权,刘新胜,黄启今.中国体视学与图像分析,2002,7(4):248-251. |
[14] | Russ John C,Dehoff Robert T.PRACTICAL STEREOLOGY,Second edition.New York:Kluwer Academic/Plenum Publisher.1-16. |
[15] | Sekita M,Haneda H,Yanagitani Y,et al.Journal of Applied Physics,1990,67(1):453-458. |
[16] | 罗谷风.结晶学导论.北京:地质出版社,1985.172-180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%