以β-磷酸三钙/硅酸钙(β-TCP/CS)纳米复合粉体为原料,制备了质量比为50∶50的β-TCP/CS复合生物陶瓷.研究表明,1150℃烧结5h得到的样品强度最好,其致密度＞96%,晶粒尺寸约120nm,强度达126MPa、同人体致密骨相当;复合陶瓷在模拟体液中浸泡1天表面就全部被类骨羟基磷灰石层覆盖住,28天的降解率达10.1%,具有良好的生物活性和降解性.研究结果显示β-TCP/CS复合生物陶瓷有望作为强度较好的可降解生物活性硬组织修复材料.
参考文献
| [1] | Klein C P A T,Groot K K D,Drissen A A,et al.Biomaterials,1985,6 (3):189-192. |
| [2] | Hench L L.J.Am.Ceram.Soc.,1991,74 (7):1487-1510. |
| [3] | 钟吉品,Hench L L(ZHONG Ji-Pin,et al).无机材料学报(Journal ofInorganic Materials),1995,10(2):129-138. |
| [4] | Hench L L,Xynos I,Edgar A,et al.无机材料学报(Journal of Inorganic Materials),2002,17(5):897-909. |
| [5] | Siriphannon P,Hayashi S,Yasumori A,et al.J.Mater.Res.,1999,14 (2):529-536. |
| [6] | Liu X Y,Ding C X,Chu P K.Biomaterials,2004,25 (10):1755-1761. |
| [7] | Lin K L,Chang J,Zhai W Y,et al.Ceram.Intern.,2005,31 (2):323-326. |
| [8] | 林开利,常江,汪正.无机材料学报(Journal of Inorganic Materials),2005,20(3):692-698. |
| [9] | Xue W C,Liu X Y,Zheng X B,et al.Biomaterials,2005,26 (17):3455-3460. |
| [10] | Xynos I D,Edgar A J,Buttery L D,et al.J.Biomed.Mater.Res.,2001,55 (2):151-157. |
| [11] | PN De Aza,Guitián F,S De Aza.Acta.Materialia,1998,46 (7):2541-2549. |
| [12] | PN De Aza,Guitián F,S De Aza.Biomaterials,1997,18 (19):1285-1291. |
| [13] | 黄翔.中国科学院上海硅酸盐研究所博士论文:生物活性硅灰石及其复合材料的研究,2002. |
| [14] | Huang X,Jiang D L,Tan S H.J.Biomed.Mater.Res.,2004,69B (1):70-72. |
| [15] | Cho S B,Nakanishi K,Kokubo T,et al.J.Am.Ceram.Soc.,1995,78 (7):1769-1774. |
| [16] | Elliott J C.Structure and Chemistry of the Apatites and Other Calcium Orthophosphates,Amsterdam:Elsevier,1994. |
| [17] | Hoeie D,Zussman.Chain Silicates,Longman,London,1963. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%