用两步法制备了(1-x)La2/3Ca1/3MnO3/xSb2O5复合样品.零场下电阻温度关系测量表明,对x＜3%范围,随Sb2O5含量增加,复合样品电阻率增大,绝缘体-金属转变温度降低;而对x＞3%范围,随Sb2O5含量增加,复合样品电阻率减小,绝缘体-金属转变温度提高.磁电阻测量表明,少量Sb2O5同La2/3Ca1/3MnO3复合,可明显增强磁电阻效应.
参考文献
| [1] | Coey J M D,Viret M,Molnar S.uon.Adv.Phys.,1999,48(2):167-293. |
| [2] | Vrnshibara A,Maxitomo Y,Arima T,et al.Phys.Rev.B.,1995,51(20):14103-14109. |
| [3] | Hwang H Y,Cheong SW,OngNP,et al.Phys.Rev.Lett.,1996,77(10):2041-2044. |
| [4] | 祝向荣,等(ZHU Xiang-Rong,et al).无机材料学报(Journal of Inorganic Materials),1999,14(6):915-920. |
| [5] | Balcells L I,Carrillo A E,Maxtinez B,et al.Appl.Phys.Left.,1999,74(26):4014-4016. |
| [6] | Petrov D K,Krusin-Elbaum L,Sun J Z,et al.Appl.Phys.Lett.,1999,75(7):995-997. |
| [7] | Koster S A,Moshnyaga V,Samwer K,et al.Appl.Phys.Left.,2002,81(9):1648-1650. |
| [8] | Yan C H,Huang Y H,Chen X,et al.J.Phys:Condens.Matter.,2002,14(41):9607-9614. |
| [9] | Gupta S,Ranjit R,Mitra C,et al.Appl.Phys.Lett.,2001,78(3):362-364. |
| [10] | Yuan S L,Xia Z C,Liu S,et al.Chin.Phys.Lett.,2002,19(8):1168-1171. |
| [11] | Huang Q,Li J,Huang X J,et al.J.Appl.Phys.,2001,90(6):2924-2929. |
| [12] | Yan C H,Xu Z G,Zhu T,et al.J.Appl.Phys.,2000,87(9):5588-5590. |
| [13] | 袁松柳,等(YUAN Song-Liu,et al).无机材料学报(Journal of Inorganic Materials),2005,20(3):623-628. |
| [14] | Huang Y H,Yan C H,Luo F,et al.Appl.Phys.Lett.,2002,81(1):76-78. |
| [15] | Yuan S L,Zhang G Q,Peng G,et al.J.Phys.:Condens.Mdtter.,2001,13(24):5691-5697. |
| [16] | Yan C H,Luo F,Huang Y H.J.Appl.Phys.,2002,91(10):7406-7408. |
| [17] | Hueso L E,Rivas J,Rivadulla F,et al.J.Appl.Phys.,1999,86(7):3881-3884. |
| [18] | Wang J,Han J T,Zhang X D,et al.Journal of Safety and Environment,2004,4(6):27-29. |
| [19] | Yuan S L,Xia Z C,Liu L,et al.Phys.Rev.B.,2003,68(18):184423-184427. |
| [20] | Yuan S L,Tang J,Liu L,et al.Europhys.Lett.,2003,63(4):433-439. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%