采用X射线衍射技术、电子背散射衍射技术和扫描电镜分别观察了不同甲烷浓度条件下沉积的CVD自支撑金刚石薄膜的宏观织构、微区晶界分布和表面形貌.研究了金刚石晶体{100}面和{111}面生长的晶体学过程.研究表明,{100}面通过吸附活性基团CH22-,而{111}面通过交替吸附活性基团CH3-和CH3-后脱氢堆积碳原子.低甲烷浓度时,{111}面表面能低于{100}面,使{111}面生长略快于{100}面.甲烷浓度升高,动力学作用增强使{100}面生长明显快于{111}面,使金刚石薄膜产生{100}纤维织构;同时显露的{100}面平行于薄膜表面,竞争生长使位于晶体侧面的{111}面由于相互覆盖而减小,形成了不同于单晶体自由生长的薄膜表面形貌组织.

参考文献

[1] 林良武,唐元洪,朱利兵(LIN liang-Wu,et al).无机材料学报(Journal of Inorganic Materials),2005,20(5):1263-1268.
[2] Yan C S,Yogesh K,Vohra M N.Diamond and Related Materials,1998,8 (12):2022-2031.
[3] Hollman P,Alahelisten A,Olsson M.Thin Solid Films,1995,270 (1):137-142.
[4] Shang N G,Lee C.Diamond and Related Materials,2000,9 (8):1388-1392.
[5] YU Z,Flodstrom A.Diamond and Related Materials,1997,6 (1):81-84.
[6] Bühler J,Prior Y.Journal of Crystal Growth,2000,209(4):779-788.
[7] Kuang Y,Badzian A,Tsong T,et al.Thin Solid Films,1996,272 (1):49-51.
[8] Sun H,Yu S,jiang Z,et al.Diamond and Related Materials,1996,5 (11):1308-1312.
[9] Yu Z,Karlsson U,Flodstron A.Thin Solid Films,1999,142 (1):74-82.
[10] Lü F X,Tang W Z,Huang T B,et al,Diamond and Related Materials,2001,10 (9):1551-1556.
[11] Evelyn M P,Graham J D,Martin L R.Diamond and Related Materials,2001,10 (9):1627-1632.
[12] Martin L R.J.Appl Phys,1991,70 (10):5667-5674.
[13] Harris S J,Belton D N.Thin Solid Films,1992,212 (1):193-200.
[14] Battle C C,Srolovitz D J,Butler J E.Journal of Crystal Growth,1998,194 (3):353-368.
[15] Maeda H,Ohtsubo K,Irke M,et al.J.Mater Res,1995,10 (12):3115-3123.
[16] Titus E,Sikder A K,Paltnikar U,et al.Diamond and related materials,2002,11 (7):1403-1408.
[17] 毛卫民,朱宏喜,陈冷,等(MAO Wei-Min,et al).无机材料学报(Journal of Inorganic Materials),2006,21(1):239-244.
[18] Chu C J,Hauge R H,Margrave J L,et al.Appl.Phys.Lett.,1992,61 (12):1393-1395.
[19] Mao W,Zhu H,Chen L,et al.Materials Science and Technology,2005,21 (12):1383-1386.
[20] Schermer J J,Theije F K,Elst W A.Journal of Crystal Growth,2002,243 (2):302-318.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%