通过热解二茂铁的工艺简便地制备了填充有α-Fe纳米线的碳纳米管(记为FCNT),铁纳米线的长度在30～500 nm之间.碳纳米管的保护作用可以使铁纳米线的抗氧化能力得到提高,测试了所得FCNT产物与石蜡组成的复合材料在2～18 GHz频段的介电谱和磁谱,并计算和测试了其吸波性能.与普通碳纳米管相比,FCNT产物的介电常数实部和虚部均有较大提高;FCNT产物的磁导率实部也比普通碳纳米管高,但虚部值在2～13GHz频段略低;FCNT吸波涂层在频率为3.5和5.0GHz处分别有两个较强的吸收峰,其强度值分别为-3.9和-4.0dB,表明这种新型吸收剂有望在2～4GHz频段实现对电磁波的有效吸收.
参考文献
| [1] | Deheer W A,Chatelain A,Ugarte D.Science,1995,270(5239):1179-1180. |
| [2] | Modi A,Koratkar N,Lass E,et al.Nature,2003,424(6945):171-174. |
| [3] | Wind S J,Appenzeller J,Martel R,et al.Applied Physics Letters,2002,80 (20):3817-3819 |
| [4] | Liu C,Fan Y Y,Liu M,et al.Science,1999,286 (5442):1127-1129. |
| [5] | Grimes C A,Mungle C,Kouzoudis D,et al.Chemical Physics Letters,2000,319 (5-6):460-464. |
| [6] | Lopez-Urias F,Munoz-Sandoval E,Reyes-Reyes M,et al.Physical Review Letters,2005,94 (21):216102-1-4. |
| [7] | Kim B M,Qian S,Bau H H.Nano Letters,2005,5 (5):873-878. |
| [8] | Karmakar S,Sharma S M,Mukadam M D,et al.Journal of Applied Physics,2005,97 (5):054306-1-5. |
| [9] | 陆国飞,包建春.电子显微学报,2005,24(4):272. |
| [10] | Che R C,Peng L M,Duan X F,et al.Advanced Materials,2004,16(5):401-405. |
| [11] | 罗发,周万城,焦桓,等(LUO Fa,et al).无机材料学报(Journal of Inorganic Materials),2003,18(3):580-584. |
| [12] | 赵东林,沈曾民(ZHAO Dong-Lin,et al).无机材料学报(Journal of Inorganic Materials),2005,20 (3):608-612. |
| [13] | Zhang X,Cao A,Wei B,et al.Chemical Physics Letters,2002,362 (3-4):285-290. |
| [14] | 赵樱.北京:清华大学硕士学位论文,2005. |
| [15] | 李聃,李泉注,张先锋,等(LI Dan,et al).无机材料学报(Journal of Inorganic Materials),2004,19(1):165-169 |
| [16] | 廖绍彬,尹光俊.宇航材料工艺,1992,2:16-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%