以油菜花粉为模板,先用超声使花粉分散在无水乙醇中,再通过水热法制备了TiO2前驱体/花粉壳-核微球;550℃焙烧脱除花粉核后得到了TiO2中空微球.采用SEM,TG,XRD,FTIR和N2吸附对TiO2前驱体/花粉壳-核微球及TiO2中空微球进行了表征.结果表明:在TiO2前驱体/花粉壳-核微球的制备过程中,超声波诱导能使TiO2前驱体较均匀的负载在花粉表面,适宜的钛酸丁酯用量为6.6 g/g花粉,适宜的水热处理温度为105℃.在此条件下得到的TiO2前驱体/花粉壳-核微球经550℃焙烧即可制得形状完整、大小约18μm的锐钛矿型TiO2中空微球.具有较窄的中孔结构,平均孔半径为1.9nm,比表面积为26.76 m2·g-1.
参考文献
| [1] | Yang H G,Zeng H C.J.Phys.Chem.B,2004,108 (11):3492-3495. |
| [2] | Li Y Z,Toyoki K,Shigenori F.J.Phys.Chem.B,2006,110 (26):13000-13004. |
| [3] | Li J,Zeng H C.Angew.Chem.Int.Ed.,2005,44 (28):4342-4345. |
| [4] | Nakamura H,Ishii M,Tsukigase A,et al.Langmuir.,2005,21 (19):8918-8922. |
| [5] | Kim K D,Kimb H T.Colloids and Surfaces A:Physicochem.Eng.Aspects,2005,255 (1-3):131-137. |
| [6] | Collins A M,Spickermann C,Mann S.J.Mater.Chem.,2003,13 (5):1112-1114. |
| [7] | Li W J,Coppens M O.Chem.Mater.,2005,17 (9):2241-2246. |
| [8] | Fujikawa S,Kunitake T.Langmuir.,2003,19 (16):6545-6552. |
| [9] | Wang L Z,Sasaki T.Chem.Mater.,2002,14 (11):4827-4832. |
| [10] | Yin J L,Chen H J,Li Z K,et al.J.Mater.Sci.,2003,38 (24):4911-4916. |
| [11] | Hall S R,Bolger H,Mann S.Chem.Commun.,2003,(22):2784-2785. |
| [12] | Hall S R,Swinerd V M,Newby F N,et al.Chem.Mater.,2006,18 (3):598-600. |
| [13] | Wang Y,Liu Z M,Han B X,et al.Langmuir,2005,21(23):10846-10849. |
| [14] | Zhang Y X,Li G,Wu Y C,et al.J.Phys.Chem.B,2005,109 (21):5478-5481. |
| [15] | 张峰,张歆(ZHANG Feng,et al).无机材料学报(Journal of Inorganic Materials),2006,21 (5):1268-1272. |
| [16] | Guo C W,Cao Y,Xie S H,et al.Chem.Commun.,2003,(6):700-701. |
| [17] | Shchukin D G,Caruso R A.Chem.Mater.,2004,16 (11):2287-2292. |
| [18] | Strohm H,Lb(o)mann P.J.Mater.Chem.,2004,14 (17):2667-2673. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%