采用脉冲激光沉积法制备了稀土掺杂钙钛矿锰氧化物Pr2/3Sr1/3MnO3(PSMO)外延薄膜,研究了薄膜在磁场、激光和电流作用下的自旋输运特性.在低温铁磁金属相,激光作用使薄膜的电阻增大,而磁场和电流则诱导电阻减小;在高温顺磁绝缘态,外场诱导均使电阻减小.在铁磁金属相,外场诱导输运特性的变化可归结于外场对体系电子自旋系统的影响:磁场和电流加强材料中eg电子和t2g局域电子间的自旋平行,增强了双交换作用;激光作用可产生光致退磁效应,减弱双交换作用.在顺磁绝缘态,场致电阻降低源于外场致使小极化子的退局域化效应.
参考文献
| [1] | Helmolt R V,Wecker J,Holzapfel B,et al.Phy.Rev.Lett.,1993,71 (14):2331-2333. |
| [2] | Jin S,Tuefel T H,Fastnacht R A,et al.Science,1994,264 (5157):413-417. |
| [3] | Jin K X,Chen C L,Wang S L,et al.J.Appl.Phys.,2004,96 (3):1537-1539. |
| [4] | 晋传贵,张涛,李晓光(JIN Chuan-Gui,et al).无机材料学报(Journal of Inorganic Materials),2007,22(2):243-246. |
| [5] | 袁松柳,方重华,缪菊红,等(YUAN Song-Liu,et al).无机材料学报(Journal of Inorganic Materials),2005,20(3):623-628. |
| [6] | Neumeier J,Hundley M F,Thompson J D,et al.Phys.Rev.B,1995,52 (10):R7006-R7009. |
| [7] | Rao C N R,Rajn A R,Ponnambalam V,et al.Phys.Rev.B,2000,61 (1):594-598. |
| [8] | Miyano K,Tanaka T,Tomioka Y,et al.Phys.Rev.Lett.,1997,78 (22):4257-4260. |
| [9] | Zhang P X,Wang J B,Zhang G Y,et al.Physica C,2001,364-365:656-658. |
| [10] | Wu T,Ogale S B,Garrison J E,et al.Phys.Rev.Lett.,2001,86 (26):5998-6001. |
| [11] | Markovich V,Rozenberg E,Yuzhelevski Y G Jung,et al.Appl.Phys.Lett.,2001,78 (22):3499-3501. |
| [12] | Gao J,Shen S Q,Li T K,et al.Appl.Phys.Lett.,2003,82 (26):4732-4734. |
| [13] | Jin K X,Chen C L,Zhao S G,et al.Materials Science and Engineering B,2006,127:285-288. |
| [14] | Ponnambalam V,Parashar S,Raju A R,et al.Appl.Phys.Lett.,1996,74 (2):206-208. |
| [15] | Parashar S,Sudheendra L,Raju A R,et al.J.Appl.Phys.,2004,95 (4):2181-2183. |
| [16] | Oshima H,Nakamura M,Miyano K.Phys.Rev.B,2001,63 (7):75111-75119. |
| [17] | Zener C.Phys.Rev.,1951,82 (3):403-405. |
| [18] | Millis A J,Shraiman Boris I,Mueller R.Phys.Rev.Lett.,1995,77 (1):175-178. |
| [19] | Roder H,Zang J,Bishop A R.Phys.Rev.Lett.,1996,76(8):1356-1359. |
| [20] | Matsuda K,Machida A,Moritomo Y.Phys.Rev.B,1998,58 (8):R4203-R4206. |
| [21] | Gehring G A,Coomber D J.J.Magn.Magn.Mater.,1998,177-181:873-874. |
| [22] | Guha A,Khare N,Raychaudhutri A K,et al.Phys.Rev.B,2000,62 (18):R11941-R11944. |
| [23] | Song X F,Lian G J,Xiong G C.Phys.Rev.B,2005,71(21):214427-214430. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%