以乙酸铈、乙酸锆为无机源,嵌段共聚物P123为模版剂,采用溶胶-凝胶法合成了介孔CeO2及CeO2-ZrO2复合体,用XRD、氮气吸附脱附、TEM、HRTEM、SAED等对材料进行了表征.结果表明,所得介孔CeO2具有规则的晶态孔道结构,孔径约在10nm左右,特别是其孔壁晶粒高度定向排列且平行于孔道方向.原位高温TEM观测表明,该介孔CeO2在800℃仍具有很高的孔道完整性.掺杂ZrO2后发现,在ZrO2摩尔含量低于30%时仍具备高度定向排列结构,高于30%时骨架晶粒取向逐渐趋向无序化.
参考文献
| [1] | Yang S W,Gao L.J.Am.Chem.Soc.,2006,128(29):9330-9331. |
| [2] | Kresge C T,Leonowicz M E,Roth W J,et al.Nature,1992,359(6397):710-712. |
| [3] | Laha S C,Ryoo R.Chem.Comm.,2003,2138-2139. |
| [4] | Wang T W,Sel O,Smarsly B.Colloid Polym Sci.,2006,285:1-9. |
| [5] | Shen W H,Dong X P,Shi J L,et al.Micropor.Mesopor.Mater.,2005,85:157-162. |
| [6] | Corma A,Atienzar P,Gareia H,et al.Nature Mater.,2004.3:394-397. |
| [7] | Brezesinski T,Antonietti M,Groenewolt M,et al.New J.Chem.,2005,29:237-242. |
| [8] | Yang P D,Zhao D Y,Margolese D I,et al.Chem.Mater.,1999,11(10):2813-2825. |
| [9] | Lee B,Lu D,Domen K,et al.Chem.Commun.,2001,2118-2119. |
| [10] | Lee B,Yamashita T,Domen K,et al.Chem.Mater.,2002,14(2):867-875. |
| [11] | Chen H R,Gu J L,Shi J L,et al.Adv.Mater.,2005,17:2010-2014. |
| [12] | Fan J,Boettcher S W,Stucky G D.Chem.Mater.,2006,18(26):6391-6396. |
| [13] | Huo C,Yu J C,Wang X,et al.J.Mater.Chem.,2005,15:2193-2198. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%