采用超声喷雾热分解工艺合成了球形锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2.考察了不同前驱溶液对粉体形貌的影响,用喷雾热分解过程机理分析了形貌差异的原因,另外研究了不同的后处理烧结时间对样品电化学性能的影响.试验结果表明,采用硝酸盐溶液经喷雾热分解制备的前驱体在900℃烧结6h可以得到电化学性能优良的正极材料,在3.0～4.3V电压区间里,首次放电容量达157.7mAh/g,40次循环后容量仍保持146.6 mAh·g-1.
参考文献
| [1] | Ohzuku T,Makimura Y.Chem.Lett.,2001,7:642-643. |
| [2] | Shaju K M,Subba Rao G V,Chowdari B V R.Electrochim.Acta,2002,48:145-151. |
| [3] | Luo X F,Wang X Y,Liao L.J.Power Source,2006,158:654-658. |
| [4] | Cho T H,Park S M,Yoshio M.J.Power Source,2005,142:306-312. |
| [5] | Chen Y,Wang G X,Konstantinov K,et al.J.Power Source,2003,119-121:184-188. |
| [6] | Lee M H,Kang Y J,Myung S T,et al.Electrochimica Acta,2004,50:939-948. |
| [7] | 胡国荣,刘智敏,方正升,等.功能材料,2005,36(03):335-339. |
| [8] | 徐志军,初瑞清,李国荣,等(XU Zhi-Jun,et al).无机材料学报(Joural of Inorganic Material),2004,19(6):1240-1248. |
| [9] | Che S L,Sakurai O,Shinozaki K,et al.J.Aerosol Sci,1998,29:271-278. |
| [10] | Messing G L,Zhang S C,Jayanthi G V.J.Am.Ceram.Soc.,1993,76 (11):2707-2719. |
| [11] | Matijevic E,Hsu W P.J.Colloid Interface Sci.,1987,118:506-523. |
| [12] | Sordelet D,Akinic M.J.Colloid Interface Sci.,1988,122:47-59. |
| [13] | Rob H S,Kang Y C,Park S B.J.Colloid Interface Sci.,2000,228:195-199. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%