采用MgCl2·6H2O为原料、KCl为助熔剂,分段灼烧制备出直径1～50 μm、长50～2000 μm的MgO晶须.通过对水氯镁石热解的理论分析、以及对灼烧各阶段产物的化学分析,确定生成晶须的中间产物为无水氯化镁,然后直接从无水氯化镁制备出MgO晶须.并探讨了MgCl2、HCl和H2O浓度的变化对晶须形貌的影响.提出了MgO晶须生长的机制:即MgO分子在容器壁上非均相成核,晶须生长的初期是以VLS机制进行,在合成的后期,VLS机制变成VS机制.
参考文献
| [1] | 周相廷,张兴利,等.河北师范大学学报(自然科学版),1997,3:76-82. |
| [2] | 李武编著.无机晶须.第一版.北京:化学工业出版社,2005.120-130. |
| [3] | Chen Y J,Li J B,Han Y S,et al.Materials Research Bulletin,2003,38 (3):445-452. |
| [4] | Chen Y J,Li J B,Han Y S,et al.Journal of Crystal Growth,2002,245 (1):163-170. |
| [5] | Hayashi S,Saito H.Journal of Crystal Growth,1974,24/25:345-349. |
| [6] | Wolff E G,Coskern T D.Journal of The American Ceramic Society,1965,48 (6):279-285. |
| [7] | Yin Yadong,Zhang Guangtao,Xia Younan.Advanced Functional Materials,2002,12 (4):293-298. |
| [8] | Ma Renzhi,Bando Yoshio.Chemical Physics Letters,2003,370 (5):770-773. |
| [9] | 王万平,张懿(WANG Wan-Ping,et al).硅酸盐学报(Journal of the Chinese Ceramic Society),2002,30(Z1):93-95. |
| [10] | Wei Zhongqing,Qi Hua,Ma Peihua,et al.Inorganic Chemistry Communications,2002,5:147-149. |
| [11] | 赵爱东,申玉双,翟学良(ZHAO Ai-Dong,et al).无机材料学报(Journal of Inorganic Materials),2005,20(1):215-219. |
| [12] | 张永键.镁硅钛,2001,(12):42-45. |
| [13] | 陈新民,张平民,叶大陆,等.中南矿冶学院学报,1980,(1):1-7. |
| [14] | 袁建君,方琪,刘智恩.材料科学与工程,1996,14(4):1-7. |
| [15] | Xia Younan,Yang Peidong,Sun Yugang,et al.Advanced Materials,2003,15 (5):353-389. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%