通过溶胶-凝胶法制备了La1-xSrxCrO3纳米粉体并实现了低温致密烧结,用X射线衍射仪、透射电镜、差示扫描量热分析仪和扫描电镜对粉体和烧结体进行分析.结果表明:粉体的平均直径＜50nm,当x=0,0.1时,粉体为单一的La1-xSrxCrO3,x=0.3时存在第二相SrCrO4.Sr掺杂使铬酸镧晶格产生畸变,随Sr含量的增加,晶格常数逐渐变小.铬酸镧纳米粉体的烧结分为两个阶段,1200℃以前的缓慢放热和1350℃左右的较快放热,分别对应烧结的初期和中期.依据DSC分析结果制订了烧结工艺,并在1380℃烧结得到相对密度91%的铬酸镧烧结体.
参考文献
| [1] | Yang Y J,Wen T L,Tu H Y,et al.Solid State Ionics.,2000,135 (1-4):475-479. |
| [2] | Yokokawa H,Sakai N,Kawada T,et al.Journal of Electrochemical Society,1991,138 (4):1018-1027. |
| [3] | Simner S,Hardy J,Stevenson J,et al.Journal of Materials Science,1999,34 (23):5721-5732. |
| [4] | Mori M,Hiei Y,Sammes N M.Solid State Ionics,1999,123 (1):103-111. |
| [5] | Mori M,Yamamoto T,Ichikawa T,et al.Solid State Ionics,2002,148 (1-2):93-101. |
| [6] | Zheng W J,Pang W Q,Meng G Y,et al.Journal of Materials Chemistry,1999,9 (11):2833-2836. |
| [7] | Rivas-Vázquez L P,Rendón-Angeles J C,RodiguezGalicia J L,et al.Solid State Ionics,2004,172 (1-4):389-392. |
| [8] | Liu X M,Su W H,Lu Z,et al.Journal of Alloys and Compounds,2000,305 (1-2):21-23. |
| [9] | Bilger S,Blass G,F(o)rthmann R.Journal of the European Ceramic Society,1997,17 (8):1027-1031. |
| [10] | Suda E,Pacaud B,Seguelong T,et al.Solid State Ionics,2002,151 (1-4):335-341. |
| [11] | Peck D H,Miller M,Hilpert K.Solid State Ionics,1999,123 (1):59-65. |
| [12] | 陈尚冰,张璐,戴向东,等.江汉石油学院学报,1995,17(4):61-64. |
| [13] | 魏智强,温贤伦,吴现成,等.兰州大学学报(自然科学版),2003,39(5):38-40. |
| [14] | 杨修春,Dubiel Manferd,Hofmeister Herbert,等.硅酸盐学报,2006,34(1):127-132. |
| [15] | 孟庆平,戎咏华,徐祖耀.中国科学E辑,2002,32(4):457-464. |
| [16] | 朱勇.科学通报,1994,39(5):169-470. |
| [17] | 李胜利,张邦强,凌子愚,等.金属热处理,2005,30(9):6-9. |
| [18] | 朱新德,李胜利,孙良成,等.金属热处理,2004,29(12):4-6. |
| [19] | 袁旭暄,贾德昌,周玉.陶瓷科学与艺术,2003,37(6):48-50. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%