对60Coγ射线辐照处理的PAN基碳纤维的力学性能、表面形貌及表面结构的变化和其与环氧树脂复合后层间剪切强度进行了初步的研究.60Coγ射线在1×102～1×103Gy辐照剂量时,使PAN基中强碳纤维本身的力学性能显著提高;使碳纤维表面的含氧官能团浓度和石墨化程度得以提高;由此制备的碳纤维环氧复合材料的层间剪切强度τILSS提高了31%左右.而在辐照剂量≥1×104Gy时,由于辐照损伤及热效应,使碳纤维的力学性能下降,增加了表面的炭化及其撕裂程度,从而减小了碳纤维环氧复合材料的层间剪切强度τILSS.
参考文献
| [1] | Hitchen S A, Ogin S L, Smith P A. Effect of fibre length on fatigue of short carbon fibre/epoxy composites. Composition,1995,26:303～308 |
| [2] | Wu G M, Schultz J M, et al. Effects of treatment on the surface composition and energy of carbon fibers. Polymer Composites, 1995,16(4):284～287 |
| [3] | Lu Y, Xue G, Wu F, et al. Pretreatment of carbon fibre and its effect on adhesion in reinforced epoxy composites. J Adhesion Sci Technol, 1996, 10(1):47～60 |
| [4] | Baillie C A, Watts J F, Castle J E, et al. The influence of chemistry on the adhesion at the interface of carbon/epoxy composites. Composite Science and Technology,1993,48:97～102 |
| [5] | Nakayama Y, Soeda F, Ishitani A. XPS study of the carbon fiber matrix interface. Carbon, 1990,28(1):21～26 |
| [6] | 许嘉敏, 李军. 碳纤维表面化学改性及其表征的研究. 高分子材料科学与工程,1990(1):66～72 |
| [7] | 满华元, 王鉴, 余宗森. 阳极氧化表面处理对碳纤维性能的影响.,1993,10(4):97～102 |
| [8] | 贺福, 王润娥. 用气相氧化法对碳纤维进行表面处理.,1988,5(1):56～61 |
| [9] | 杨永岗, 贺福, 王茂章, 等. 碳纤维表面处理及其评价. 材料研究学报,1996,10(5):460～466 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%