分别采用测量ENF试样加载点位移与测量其端部剪切位移CSD(Crack Shear Displacement)的试验方法,研究了缝合复合材料层合板的II型层间断裂韧性以及缝合密度,缝合线的直径等缝合参数对于缝合复合材料层合板II型层间断裂韧性和分层模式的影响.结果表明,缝合降低了层合板初始分层韧性GIIi,但对于分层的扩展有良好的抑制作用.缝合参数对此有较大影响.

Effects of through-thickness stitching on Mode II interlaminar fracture toughness(GII) and modes of delamination of composite laminates were investigated by performing end-notched flexure(ENF) tests. Vertical displacement of loading point and crack shear displacement(CSD) between upper and lower crack surfaces at the end of ENF specimens were measured. Different stitch yarns and stitch densities were considered. The addition of stitching was found to decrease the initiation interlaminar fracture toughness GIIi, but can effectively suppress the growth of delamination.

参考文献

[1] Carlsson L A, Gillespie J W, Jr. Pipes R B. On the analysis and design of the End Notched Flexure(ENF) specimen for mode II testing[J]. J of Composite Materials, 1986, 20(6): 595-604.
[2] 中国航空研究院. 复合材料飞机结构耐久性/损伤容限设计指南[M]. 北京:航空工业出版社, 1995.
[3] Sailendra N Chatterjee. Analysis of test specimens for interlaminar mode II fracture toughness, Part 1. Elastic Laminates[J]. J of Composite Materials, 1991, 25(5):470-493.
[4] Timoshenko S P, Goodier J N. Theory of Elasticity[M]. New York: McGraw-Hill, 1970.325-328.
[5] Brain Cox, Roberta Massabo, Daniel Mumm, Andre Tuettini, Keith Kedward. Delamination fracture in the presence of through-thickness reinforcement[A]. Proceedings of ICCM-11[C]. Gold Coast, Australia, 1997.1159-1177.
[6] Master J E. Correlation of impact and interleaf delamination resistance in interleafed laminates[A]. Matthews F L, Busskell N C R, Hodgkinson J M, J Morton. Proc. Sixth Int. Conf. On Composite Materials/Second European Conf. On Composite Mater[C]. Elsevier Applied Science Publ Ltd, 1987. 96-107.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%