对[±20°]钢丝帘线橡胶复合材料在拉伸循环载荷下的疲劳特性进行了试验研究,分析了最大应力、加载频率对材料疲劳寿命的影响以及疲劳过程中的滞后损失和温升,根据疲劳寿命图得到了线性寿命预报方程.研究表明,在载荷控制下该材料的疲劳过程呈现明显的三阶段规律,两步等幅加载实验证明这一规律同样适用于有损试件的疲劳过程.
参考文献
| [1] | Crosch K. Rolling resistance and fatigue life of tires[J]. Rubber Chemistry and Technology, 1988, 61(1): 42-63. |
| [2] | 谭惠丰.柔性复合材料双重非线性层合理论[D].哈尔滨:哈尔滨工业大学,1997.4. |
| [3] | Lake G J. Mechanical fatigue of rubber[J]. Rubber Chemistry and Technology, 1972, 45(1): 307-328. |
| [4] | Young D G. Fatigue and fracture of elastometric materials[J].Rubber World, 1991, 3: 30-34. |
| [5] | Hamed G R. Molecular aspects of the fatigue and fracture of rubber[J]. Rubber Chemistry and Technology, 1994, 67 (3): 529-535. |
| [6] | Forster M J, Perttyman L B. A new improved tirecord fatigue tester[J]. Rubber Chemistry and Technology, 1969, 42 (4):1000-1008. |
| [7] | Causa A G. Fatigue testing of polymeric reinforcing cords[J]. Tire Technology International, 1996,63 ( 3 ): 1101 - 1103. |
| [8] | Pokluda I. Fatigue of steel cords[J]. Kautsch Gummi Kunstst,1989, 42(5): 410-414. |
| [9] | 刘宇艳.橡胶复合材料的疲劳[D].哈尔滨:哈尔滨工业大学,1998.34-102. |
| [10] | 刘宇艳,万志敏,田振辉,等.单向聚酯帘线增强橡胶材料疲劳特性研究[J].复合材料学报,1998,1 5(4):97-101. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%