报道了聚苯乙烯辐射接枝纳米二氧化硅微粒(SiO2-g-PS)填充聚丙烯(PP)的增强增韧作用,并从界面效应和逾渗行为的角度对此类复合材料的力学行为进行了分析.结果表明,接枝纳米微粒填充入聚合物时所形成的微粒/聚合物复合颗粒可以整体发挥协同作用,带来较强的界面效应,并有可能导致双逾渗行为,从而有利于发挥纳米微粒的特殊性能.

参考文献

[1] Giannelis E P. Polymer layered silicate nanocomposites [J]. Adv Mater, 1996, 8(1): 29-35.
[2] Carrotenuto G, Nicolais L, Kuang X, et al. A method for the preparation of PMMA-SiO2 nanocomposites with high homogeneity [J]. Appl Comp Mater, 1995, 2: 385.
[3] 容敏智,章明秋,曾汉民,等. 纳米无机粒子增韧增强塑料及其制备方法 [P].中国专利:CN99116017,1999.
[4] Rong M Z, Zhang M Q, Zeng Y X, et al. Structure-property relationships of irradiation grafted nano-inorganic particle filled polypropylene composites [J]. Polymer ,2001,42(1):161-183.
[5] Rong M Z, Zhang M Q, Zeng Y X, et al. Irradiation graft polymerization on nano-inorganic particles: an effective means to design polymer based nanocomposites [J]. J Mater Sci Lett, 2000, 19(13): 1159-1161.
[6] 周维祥. 塑料测试手册[M]. 北京:化学工业出版社,1987. 126-128.
[7] Ahmed S, Jones F R. A review of particulate reinforcement theories for polymer composites [J]. J Mater Sci, 1990, 25: 4933-4942.
[8] Jancar J, Dianselmo A, Dibenedetto A T. The yield strength of particulate reinforced thermoplastic composites [J]. Polym Eng Sci, 1992, 32: 1394-1399.
[9] Nicolais L, Narkis M. Stress-strain behavior of styrene-acrylonitrile/glass bead composites in the glass region [J]. Polym Eng Sci, 1971, 11: 194-199.
[10] Wu S. Phase structure and adhesion in polymer blends: a criterion for rubber toughening [J]. Polymer, 1985, 26: 1855-1863.
[11] 漆宗能. 高聚物的增韧. 见:高新技术新材料要览(曾汉民主编)[M]. 北京:中国科学技术出版社,1993. 492-498.
[12] Fu Q, Wang G. Polyethylene toughened by CaCO3 particles-percolation model of brittle-ductile transition in HDPE/CaCO3 blends [J]. Polym Int, 1993, 30: 309-312.
[13] Friedrich K. Microstructural efficiency and fracture toughness of short fiber/thermoplastic matrix composites [J]. Comp Sci Technol, 1985,22:43-74.
[14] Zallen R. The Physics of Amorphous Solids [M]. New York: Wiley, 1983.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%