对电子束辐射固化的环氧树脂进行了动态力学分析.通过对不同样品凝胶含量、内耗tanδ及动态模量变化趋势的研究,得到电子束辐射剂量、引发剂用量和热处理等因素对环氧树脂辐射交联反应的影响规律.辐射剂量的增加使环氧树脂凝胶含量、玻璃化温度Tg及高温模量有所增加,但增长幅度在高辐射剂量下逐渐变小,且树脂交联体系的不均匀性随辐射剂量增大而有所增加.低剂量辐射下,环氧树脂固化物的玻璃化温度及高温模量随引发剂用量增加而增大,高辐射剂量下,引发剂的用量存在最佳值.经过热处理后辐射样品的交联程度得到提高,当热处理温度超过引发剂的热分解温度时,树脂体系中会存在因热固化反应而形成的局部交联网络.
参考文献
| [1] | Parrot P, His S, Boursereau F. Electron beam cured composites [J]. International SAMPE Symposium and Exhibition Proceedings, 1999, 44: 1354-1358. |
| [2] | Crasto A S, Kim R Y, Rice B P. Electron beam cure of composites for aerospace structures [J]. International SAMPE Symposium and Exhibition Proceedings, 1997, 42: 487-497. |
| [3] | Abrams F and Tolle T B. An analysis of E-beam potential in aerospace composite manufacturing [J]. International SAMPE Symposium and Exhibition Proceedings, 1997, 42: 548-557. |
| [4] | Charlesby A. Atomic Radiation on Polymers [M]. Oxford: Pergamon Press, 1960. |
| [5] | Chapiro A. The contribution of Arthur Charlesby to the radiation chemistry of polymers-personal experience [J]. Rad Phys Chem, 1998, 51(1): 6-9. |
| [6] | Chapiro A. Radiation Chemistry of Polymeric Systems [M]. New York: Interscience, 1962. |
| [7] | Saunders C B, Lopata V J, Kremers W, et al. Electron curing of fibre-reinforced composites: An industrial application for high-energy accelerators [J]. Rad Phys Chem, 1995, 46(4-6): 991-995. |
| [8] | Saunders C B, Singh A, Lopata V J, et al. Radiation processing of fibre-reinforced composites [J]. ACS Symp Ser, 1993, 527: 305-310. |
| [9] | Singh A, Saunders C B, Barnard J W, et al. Electron processing of fibre-reinforced advanced composites [J]. Rad Phys Chem, 1996, 48(2): 153-170. |
| [10] | Crivello J V, Walton T C, Malik R. Fabrication of epoxy matrix composites by electron beam induced cationic polymerization [J]. Chem Mater, 1997, 9: 1273-1284. |
| [11] | Crivello J V. UV and electron beam-induced cationic polymerization [J]. Nucl Instr and Meth, 1999, B151: 8-21. |
| [12] | Beringer F M, Drexler M, Gindler E M, et al. Diaryliodonium salts Ⅰ: Synthesis [J]. J Am Chem Soc, 1953, 75(5): 2705-2708. |
| [13] | Fouassier J P, Rabek J F. Radiation curing in polymer science and technology--Fundamentals and methods Vol.1 [M]. London: Elsevier Science Publishers LTD, 1993. |
| [14] | Anseth K S, Bowman C N, Peppas N A. Dynamic mechanical studies of the glass transition temperature of photopolymerized multifunctional acrylates [J]. Polymer Bulletin, 1993, 31: 229-233. |
| [15] | Glauser T, Johansson M, Hult A. Electron-beam curing of thick thermoset composite matrices [J]. Polymer, 1999, 40: 5297-5302. |
| [16] | Sui G, Zhang Z G, Zhong W H, et al.Research on Electron Beam Curing of Bisphenol A Epoxy Resins [A]. In: Zhang R, ed. The Proceeding of 13th International Conference on Composite Materials [C]. Beijing: Academic Publisher, 2001. 217-226. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%