采用竖式炉流动法制备的碳纳米管经液相阳极氧化表面处理后增强ABS热塑性工程塑料.复合材料的力学性能研究显示:碳纳米管的加入有效提高了复合材料的拉伸性能,但材料的耐冲击性能下降.当碳纳米管含量为12 wt%时,复合材料的拉伸强度由45.00 MPa提高到69.96 MPa,杨氏模量由0.75 GPa提高到1.93 GPa.对碳纳米管/ABS复合材料的反射系数测定表明:复合材料在一定频率范围内有雷达波吸收性能.
参考文献
| [1] | Iijima S. Helical microtubules of graphitic carbon [J]. Nature, 1991, 354(6348): 56-58. |
| [2] | Liu Jie, Rinzler Andrew G, Dai Hongjie, et al. Fullerene pipes [J]. Science, 1998, 280(5367): 1253-1255. |
| [3] | Ajayan P M. Nanotubes from carbon [J]. Chem Rev, 1999, 99(7): 1787-1799. |
| [4] | Li W Z, Xie S S, Qian L X, et al. Large-scale synthesis of aligned carbon nanotubes [J]. Science, 1996, 274(5293): 1701-1703. |
| [5] | 张立德,牟季美.纳米材料和纳米结构 [M]. 北京:北京科学出版社, 2001. 28-33. |
| [6] | Dillin A C, Jones K M, Bekkedahl T A, et al. Storage of hydrogen in single-doped carbon nanotubes [J]. Nature, 1997, 386(6623): 377-379. |
| [7] | Wu G T, Wang C B, Zhang X B, et al. Structure and lithium insertion properties of carbon nanotubes [J]. Journal of the Electrochemical Society, 1999, 146(5): 1696-1701. |
| [8] | 沈曾民, 赵东林. 镀镍碳纳米管的微波吸收性能研究 [J]. 新型炭材料, 2001, 16(1): 1-3. |
| [9] | Frankland Sarah-Jane, Brenner Donald W. Materials applications of carbon nanotubes: hydrogen storage and polymer composites [J]. Polym Prepr, 1999, 40(2): 721-722. |
| [10] | Yakobson B I, Brabec C J, Bernholc J. Nanomechanics of carbon tubes: Instabilities beyond linear response [J]. Phys Rev Lett, 1996, 6(14): 2511-2514. |
| [11] | Salvetat Jean-Paul, Briggs G Andrew D, Bonard Jean-Marc, et al. Elastic and shear moduli of single-walled carbon nanotubes ropes [J].Phys Rev Lett, 1999, 82(5): 944-947. |
| [12] | Treacy M M J, Ebbesen T W, Gibson J M. Exceptionally high Young's modulus observed for individual carbon nanotubes [J]. Nature, 1996, 381(6584): 678-680. |
| [13] | Jin L, Bower C, Zhou O. Alignment of carbon nanotubes in a polymer matrix by mechanical stretching [J]. Appl Phys Lett,1998, 73(9): 1197-1199. |
| [14] | Schadler L S, Giannaris S C, Ajayan P M. Load transfer in carbon nanotube epoxy composites [J]. Appl Phys Lett, 1998, 73(26): 3842-3844. |
| [15] | Kuzumaki T, Mjyazawa K, Ichinose H, et al. Processing of carbon nanotube reinforced aluminum composite [J]. J Mater Res, 1998, 13(9): 2445-2449. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%