以多层机织布为对象,首先基于两个分别对应于两种典型叠加模式的单元结构模型,通过理论分析,建立了多层机织布纵向切面内气泡形成的分析模型;然后采用有限元-控制体积方法对单元结构内树脂的扩散及气泡形成的过程进行了数值模拟.理论分析和数值模拟的结果符合一致,均表明:不同局部区域差异很大的渗透系数是气泡形成的最根本原因,而纬线的轴向渗透系数和经线的横向渗透系数之比对多层机织布纵向切面内气泡的形成及尺度起着决定性的作用.
参考文献
| [1] | Harper B D, Staab G H, Chen R S. A note on the effects of voids upon the hygral and mechanical properties of AS4/3502 [J]. Journal of Composite Materials, 1987, 21:280-289. |
| [2] | Bowles K J, Frimpong S. Void effects on the interlaminar shear strength of unidirectional graphite-fiber-reinforced composites [J]. Journal of Composite Materials, 1991, 26:1487-1509. |
| [3] | Parnas R S, Phelan Jr F R. The effect of heterogenous porous media on mold filling in resin transfer molding [J]. SAMPE, 1991, 22:53-60. |
| [4] | Chen Y T, Davis H T, Macosko C W. Wetting of fiber mats for composites manufacturing: Ⅰ. Visualization experiments [J]. AICHE Journal, 1995, 41(10):2261-2281. |
| [5] | Chan A W, Morgan R J. Sequential multiple port injection for resin transfer moulding of polymer composites [J]. SAMPE, 1992, 23:45-49. |
| [6] | Patel N, Lee L J. Effects of fiber mat architecture on void formation and removal in liquid composite molding [J]. Polymer Composites, 1995,16(5):386-399. |
| [7] | Patel N, Rohatgi N, Lee L J. Micro scale flow behavior and void formation mechanism [J]. Polymer Engineering and Science, 1995, 35(10): 837-851. |
| [8] | Rohatgi V, Patel N, Lee L J. Experimental investigation of flow-induced microvoids during impregnation of unidirectional stitched fiberglass mat [J]. Polymer Composites, 1996, 17:161-170. |
| [9] | Binetruy C, Hilaire B. Tow impregnation model and void formation mechanisms during RTM [J]. Journal of Composite Materials, 1998, 32(3):223-245. |
| [10] | Kang M K, Lee W I, Hahn H T. Formation of microvoids during resin-transfer molding process [J]. Composites Science and Technology, 2000, 60:2427-2434. |
| [11] | 尹明仁,段跃新,李丹,等. 视窗化RTM工艺充模过程模拟仿真技术研究 [J]. 复合材料学报,2001,18(4):17-22. |
| [12] | Yu B, Lee L J. A simplified in-plane permeability model for textile fabrics [J]. Polymer Composites, 2000, 21(5):660-685. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%