采用LAS玻璃粉末和激光诱导法制备的纳米SiC(N)粉体,通过热压烧结法制备了SiC(N)/LAS纳米陶瓷复合材料,研究了该复合材料在8.2～12.4 GHz频率范围内的微波介电特性.结果表明,SiC(N)/LAS的介电常数主要受纳米SiC(N)粉体含量的控制,此外还与烧结温度有关.随着烧结温度的提高,复合材料介电常数和介电损耗均随之增大.SiC(N)/LAS对电磁波的损耗作用明显优于同体积分数的纳米SiC(N)与石蜡混合体,这与烧结过程中形成的碳界面有关.
参考文献
| [1] | Rawlings R D. Glass-ceramic matrix composites [J]. Composite, 1994, 25(5): 372-379. |
| [2] | Hsu J Y, Speyer R F. Fabrication and properties of SiC fiber-reinforced Li2O?Al2O3*6SiO2 glass-ceramic composites [J]. J Mater Sci, 1992, 27: 381-390. |
| [3] | Prewo K M, Brennan J J. Silicon carbide yarn reinforced glass matrix composites [J]. J Mater Sci, 1982, 17:1201-1206. |
| [4] | 罗发,周万城. Si2ON2/LAS纳米复合材料的制备与性能研究 [J]. 材料工程,2001 (7):22-24. |
| [5] | Toshikatsu I. Recent development of the SiC fiber Nicalon and its composite, including properties of the Hi-Nicalon for ultra high temperature [J]. Composite Sci Tech, 1994, 51:135-141. |
| [6] | 麦克米伦 W P. 微晶玻璃 [M]. 北京:中国建筑工业出版社,1988.232. |
| [7] | 罗发,周万城,赵东林. 结构吸波材料中纤维的电性能和吸波性能 [J].材料工程,2000 (1):37. |
| [8] | HSU J Y, SPEYER R F. Interfacial phenomenology of SiC fiber reinforced Li2O*Al2O3*6SiO2 glass-ceramic composites [J]. J Mater Sci, 1992, 27:374-380. |
| [9] | 王相元,钱鉴,朱航飞,等. 非磁性吸收剂构成的单层吸波材料性能分析 [J].隐身技术,2000 (1):14-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%