合成了一种耐湿热性能优异的环氧树脂9,9-二[4-(2,3-环氧丙氧基)苯基]芴,通过对环氧化反应影响因素的讨论确定了最佳的环氧化反应条件,使产物环氧值达到了理论值的97 %.确定了纯的9,9-二[4-(2,3-环氧丙氧基)苯基]芴环氧树脂的固化工艺,并对其树脂浇注料的力学性能进行了评测.为研究9,9-二[4-(2,3-环氧丙氧基)苯基]芴对其它环氧树脂体系湿热性能的影响,对9,9-二[4-(2,3-环氧丙氧基)苯基]芴/AG-80树脂体系的吸水率进行了测定,并比较了该体系吸水前后玻璃化转变温度和模量的变化,从而证明了9,9-二[4-(2,3-环氧丙氧基)苯基]芴对提高环氧树脂耐湿热性能的作用.
参考文献
[1] | Schlaudt L M. Toughenable Epoxy Resin for Elevated Temperature Applications [A]. In: Zakrzewski G A,ed. The 34th International SAMPE Symposium(May 8-11) [C]. Covina Calif: SAMPE, 1989. 917-920. |
[2] | Schultz W J. Glycidylethers of Fluorene-Containing Bisphenols [P]. US Pat: 4707534, 1987-11-17. |
[3] | Almer. Improved Epoxide Resin Compositions and Method [P]. Eur Pat: 0325058B1, 1989-7-26. |
[4] | John E. Process for Purification of 9,9-Bis-hydroxy-Phenyl-fluorene [P]. US Pat: 4024194. 1977-5-17. |
[5] | Siaboles O. Condensation Process [P], US Pat: 4467122. 1984-8-21. |
[6] | Rohm Gmbh. Verfahren für Herstellung von 9,9-Bis-(4-Hydrixu Phenyl)-Fluorene [P], DE Pat: 34 39 484A1, 1986-5-7. |
[7] | Mormarm W. Liquid crystalline thermosets from triaromatic ester group containing diepoxides and aromatic diamines [J]. Macromli Chem Phys, 1998, 199: 853-859. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%