用扫描电镜(SEM)背散射成像技术对Zr变质SiCp/ZA27复合材料在部分重熔过程中的组织演变进行了研究,并与未变质复合材料及基体合金作了对比.结果表明:经0.2 wt%Zr变质的SiCP/ZA27复合材料在460C加热过程中(0min～30min),其基体组织依次经历了晶臂的快速合并,晶粒的长大,晶界区域的熔化、组织分离,最后经球状化形成触变成形所需的粒径较为均匀、细小、圆整的半固态浆料,在随后的保温过程中(30 min～80min)未发现明显的粗化现象;未变质复合材料则形成相互连接的不规则组织,即使经长时间的保温(80 min),也未全部球状化;基体合金组织的分离快于变质复合材料,但在保温中的晶粒粗化却较为严重.加热初期晶粒的快速粗化是由共晶组织向晶内的迅速扩散引起的.本文作者从相变角度分析了组织的演变过程.
参考文献
| [1] | 陈体军,郝远.铸造锌基复合材料的研究现状[J].材料导报,2000,14(3):29-31. |
| [2] | Mathukumarasumy S, Buni S Y, Seshan S. ZA27 alloy-based cast MMCs with ceramic reinforcement [J]. AFS Trans,1994, 102:819-824. |
| [3] | 陈体军,郝远.金属的半固态成形技术与应用[J].铸造,2001,50(11):645-649. |
| [4] | Hong T W, Kim S K, Ha H S, et al. Microstructural evolution and semisolid forming of SiC particulate reinforced AZ91DHP magnesium composites [J]. Mater Sci Technol,2000, 16(7-8): 887-892. |
| [5] | Kim S K, Kim Y J. Microstructural evolution and thixoformability of semi-solid SiCP/AZ91D Mg composites [J]. Mater Trans, 2002, 42(7): 1277-1283. |
| [6] | 陈体军,郝远,寇生中,等.机械搅拌对ZA27合金微观组织的影响[J].甘肃工业大学学报,1997,23(1):27-30. |
| [7] | 陈体军,郝远,陆松,等.ZA27合金在SIMA处理过程中应变量和等温温度对组织的影响[J].金属热处理学报,2000,21 (1) :26-31. |
| [8] | Chen T J, Hao Y, Ma Y, et al. Structural evolution of ZA27alloy during semi-solid isothermal heat treatment [J]. Trans Nonferrous Met Soc China, 2001, 11(1) :98-102. |
| [9] | Chen T J, Hao Y, Sun J. Microstructural evolution of previously deformed ZA27 alloy during partial remehing [J].Mater Sci Eng, 2002, 337A(1-2): 73-81. |
| [10] | 陈体军,郝远,狄杰建,等.变质剂对ZA27合金半固态等温热处理组织的影响[J].热加工工艺,2001,(4):23-25. |
| [11] | 陈体军,郝远,孙军,等.ZA27合金部分重熔过程中组织的扫描电镜观察[J].材料科学与工程,2002,20(1):47-50. |
| [12] | 郝远,陈体军,马颖.SiCP/ZA27复合材料的制备及其力学性能[J].特种铸造及有色合金,1997,(2):25-28. |
| [13] | 陈体军,郝远,孙军,等.ZA27合金铸态组织的研究[J].中国有色金属学报,2002,12(2):294-299. |
| [14] | Tzimas E, Zavaliangos A. Evolution of near-equiaxed microstructure in the semi-solid state [J]. Mater Sci Eng,2000, A289(1-2): 228-240. |
| [15] | Li Z Q, Zhang S Y, Wu B Y. Solidification and microstructure of ZA27/SiCP composite fabricated by mechanical-electromagnetic combination stirring process [J]. Mater Sci Technol, 2001, 17(4): 465-471. |
| [16] | 祝要民,谢敬佩,李晓辉,等.SiCP/ZA27复合材料界面微观分析及高温蠕变性能[J].复合材料学报,2002,19(4):42-45. |
| [17] | Fan T X, Shi Z L, Zhang D, et al. The melt structures above the liquidus in SiCP/Al composite [J]. J Mater Sci, 1999, 34(1):59-64. |
| [18] | Fan T X, Shi Z L, Zhang D, et al. The interfacial reaction characteristics in SiC/Al composite above liquidus during remelting [J]. Mater Sci Eng, 1998, A257(2) :281-286. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%