详细研究了聚氯乙烯(PVC)、氯化聚乙烯(CPE)和纳米碳酸钙(Nano-CaCO3)的三元复合体系的加工工艺和组成变化与力学性能之间的关系.研究表明:如果先将CPE等弹性体和纳米CaCO3制成母粒,然后再与PVC进行混合,有利于纳米粒子在基体中的分散,在复合体系中,纳米CaCO3和CPE达到了协同增韧PVC的作用,同时,纳米CaCO3具有补强作用,且当母粒的组成为CPE/纳米CaCO3=1∶2时,对PVC改性效果最佳.
参考文献
[1] | Zárraga A, Pea J J,Muoz M E,et al. Thermorheological Analysis of PVC Blends [J].Polymer Science,2000,38(3):469-477. |
[2] | 欧玉春.刚性粒子填充聚合物的增强增韧与界面相结构 [J].高分子材料科学与工程,1998,14(2):12-15. |
[3] | Demjén Z, Pukánszky B,Nagy J.Evaluation of interfacial interaction in polypropylene/surface treated CaCO3 composites [J].Composites Part A,1998,29(3):323-329. |
[4] | Anya C C.Microstructural nature of strengthening and toughening in Al2O3-SiC(p) nanocomposites [J].Materials Science,1999,34(22):5557-5567. |
[5] | Balazs A C,Singh C, Zhulina E,et al.Modeling the Phase Behavior of Polymer/Clay Nanocomposites [J].Acc Chem Rec,1999,32(8):651-657. |
[6] | Jancar J, Dibenedtd A T.The mechanical properties of ternary composites of polypropylene with inorganic fillers and elastomer inclusions [J].Materials Science,1994,29(17):4651-4658. |
[7] | Emphet P R,Horanont P.Influence of stearic acid treatment of filler particles on the structure and properties of ternary-phase polypropylene composites [J].Applied Polymer Science,1999,74(14):3445-3454. |
[8] | 容敏智,章明秋,郑永祥,等.纳米SiO2增韧增强聚丙烯的界面效应与逾渗行为[J].复合材料学报,2002,19(1):1-4. |
[9] | 张维虎.对CPE改性硬PVC的探讨 [J].聚氯乙烯,1998,(5):31-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%