利用TEM对Fe3Al/Al2O3复合材料的位错形貌进行了观测分析,观察到Fe3Al/Al2O3中丰富的位错组态.根据透射电镜观察,引入Fe3Al后,Al2O3晶内产生大量位错,位错多产生于Fe3Al于Al2O3相界面附近,亚界面的形成使基体晶粒再细化,使强度提高.在Fe3Al中观察到超点阵位错,对材料起到"有序强化"作用.
参考文献
[1] | 吕王君,郑潘祥,金志浩.氧化铝基陶瓷复合材料的阻力曲线行为及其抗热震性能 [J].复合材料学报,2001,18(4): 76-81. |
[2] | Xu D S, Yeomans J A. Microstructure and fracture toughness of nickel particle toughened alumina matrix composites [J]. J Mater Sci,1996,31: 875-880. |
[3] | Loehman R E, Ewsuk K, Tomsia A P. Synthesis of Al2O3-Al composites by reactive melt penetration [J]. J Am Ceram Soc, 1996,79:27-32. |
[4] | Aldrich D E, Edirisinghe M T. Addition of copper particles to alumina matrix [J]. Journal of Materials Science Letters, 1998,17(12):965-967. |
[5] | Guichard J L, Tillement O, Mocellin A. Alumina-chromium cermets by hot-pressing of nanocomposites [J]. J Eur Ceram Soc, 1998,18:1743-1752. |
[6] | 龚红宇,尹衍升,李爱菊.反应烧结法制备(AlN,TiN)-Al2O3复合材料的研究 [J].复合材料学报,2003,20(1):16-21. |
[7] | 张虎,张二林,高之理,曹松岩.Ti-40Al-2B合金微观组织和初生TiB2生长特性 [J].复合材料学报,2001,18(4):47-49. |
[8] | 刘伯威,潘进,樊毅,等.SiC颗粒强韧化MoSi2复合材料 [J].复合材料学报,2002,19(1):59-63. |
[9] | Rodel J, Prioelipp H, Claussen N, et al. Ni3Al/Al2O3 composites with interpenetrating networks [J]. Sripta Metallurgica et Materialia, 1998, 33(5): 843-848. |
[10] | Tuan W H. Toughening alumina with nickel aluminide inclusions [J]. J Eur Ceram Soc, 2000, 20:895-899. |
[11] | Chou W B, Tuan W H, Chang S T. Preparation of NiAl toughened Al2O3 by vacuum hot pressing [J].British Ceramic Transactions, 1996, 95(2): 71-74. |
[12] | Niihara K. New design concept of structural ceramics [J]. J Ceram Soc Jpn, 1991, 99(10): 974-982. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%