研究了SiC涂层连续碳纤维增韧的SiC基复合材料(SiC-C/SiC)在低频拉-拉循环应力下,干氧环境、水蒸气环境、湿氧环境以及含硫酸钠蒸气环境中,1000℃、1200℃和1300℃高温下的应力氧化与应力腐蚀情况.通过比较复合材料在相同循环应力条件下、不同温度和环境中的寿命,揭示了复合材料在高温、循环应力状态下的腐蚀机理.研究发现,在循环应力状态下,氧气是导致SiC-C/SiC复合材料寿命下降的主要因素.1000℃
参考文献
[1] | 美国空军技术学院. 中国航空信息中心研究部译. 国防关键技术[M]. 北京: 中国航空信息中心, 1994. 5. |
[2] | Lamouroux F, Bourrat X, Naslain R, et al. Structure/oxida-tion behavior relationship in the carbonaceous constituents of 2D-C/PyC/SiC composites [J]. Carbon, 1993, 31(8): 1273-1288. |
[3] | Lamouroux F, Naslain R, Jouin J M. Kinetics and mechani-sms of oxidation of 2D woven C/SiC composites Ⅱ:Theoretical approach[J]. J Am Ceram Soc, 1994, 77(8):2058-2068. |
[4] | Lamouroux F, Camus G, Thébault J. Kinetics and mechani-sms of oxidation of 2D woven C/SiC compositesⅠ: Experimental approach[J]. J Am Ceram Soc,1994, 77(8):2049-2057 . |
[5] | Yin X, Cheng L, Zhang L, et al. Behaviour of three-dimen-sional woven C/SiC composites [J]. Mater Sci Tech, 2001, 17:727-730. |
[6] | Yin X, Cheng L, Zhang L, et al. Oxidation behavior of 3D C/SiC composites in two oxidizing environments [J]. Compos Sci Technol, 2001,61: 977-980. |
[7] | Cheng L, Xu Y, Zhang L, et al. Oxidation and defect control of CVD SiC coating on three-dimensional C/SiC composites [J]. Carbon, 2002, 40(12): 2229-2234. |
[8] | 栾新刚.高温腐蚀环境SiC-C/SiC的性能演变规律与损伤机理[D].西安:西北工业大学,2002. |
[9] | Luan X, Cheng L, Yin X. Corrosion of a SiC-C/PyC/SiC composite by sodium sulfate vapor at high temperatures [J]. Sci Eng Compos Mater, 2002, 10(2): 157-162. |
[10] | Luan X, Cheng L. Corrosion of a SiC-C/SiC composite in environments with Na2SO4 vapor and oxygen [J]. Sci Eng Compos Mater,2002, 10(4): 261-266. |
[11] | Halbig M C, Brewer D N, Eckel A J, et al. Stressed oxidation of C-SiC composites[R]. NASA/TM-1997-107457. New York: NASA, 1997. |
[12] | Halbig M C, Brewer D N, Eckel A J. Degradation of Conti-nuous Fiber Ceramic Matrix Composites under Constant-Loaded Conditions[R]. TM-2000-209681.New York: NASA, 2000. |
[13] | Halbig M C, Eckel A J. Oxidation of Continuous Carbon Fibers within a Silicon Carbide Matrix under Stressed and Unstressed Conditions[R]. TM-2000-2100224. New York: NASA, 2000. |
[14] | Halbig M C, Eckel A J, Cawley J D. Oxygen Diffusion and Reaction Kinetics in Continuous Fiber Ceramic Matrix Composites[R]. TM-1999-208911. New York: NASA, 1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%