研究了由GF/PP复合纱编织而成的1+1罗纹针织物预型件的线圈密度对热压成型后的玻璃纤维针织物增强聚丙烯复合材料拉伸性能的影响.对6种由不同线圈密度的GF/PP复合纱1+1罗纹针织物预型件经热压得到的复合材料进行的拉伸性能测试研究表明:随着复合纱针织物预型件线圈密度的逐渐增大,复合成型后的复合材料的拉伸强度先逐渐增大,而后稍有降低;断裂伸长的变化趋势则恰恰相反.光学显微镜和扫描电镜照片研究表明:随着针织物预型件线圈密度的增大,成型后的复合材料的空隙率减小,纤维/基体分布更加均匀;与此同时,线圈的曲率半径减小,玻璃纤维脆断现象加剧.
参考文献
| [1] | Hou M, Ye L, Mai Y M. Review-advances in processing of continuous fibre reinforced composites with thermoplastic matrix [J]. Plastics, Rubber and Composites Processing and Applications, 1995, 23(5): 279-293. |
| [2] | Miller A H, Dodds N, Hale J M, et al. High speed pultrusion of thermoplastic matrix composites [J]. Composites Part A,1998, 29(5): 773-782. |
| [3] | Nowacki J, Neitzel M. Thermoforming of reinforced thermoplastic stiffened structure [J]. Polymer Composites, 2000,21(4): 531538. |
| [4] | Svensson N,Shishoo R. Manufacturing of thermoplastic composites from commingled yarns: A review [J]. Journal of Thermoplastic Composite Materials, 1998, 11(1): 22-56. |
| [5] | Shonaike G O, Hamada H, Maekawa Z, et al. The influence of cooling conditions on the mechanical properties of commingled yarn composites [J]. Journal of Thermoplastic Composite Materials, 1996, 9(1): 76-89. |
| [6] | Long A C, Wilks C E, Rudd C D. Experimental characterization of the consolidation of a commingled glass/polypropylene composite [J ]. Composites Science and Technology, 2001, 61: 1591-1603. |
| [7] | 余剑英,周祖福.连续纤维增强热塑性复合材料的制备成型技术及其应用前景[J].武汉工业大学学报,1998,20(4):22-24,31. |
| [8] | 吴学东,丁辛.热塑性树脂及复合材料用摩擦纺混纤纱[J].玻璃钢/复合材料,1997(4):5-7. |
| [9] | 马满珍,孙亮,翁永华.空气变形纱预浸渍技术对连续玻璃纤维/涤纶复合材料力学性能的影响[J].玻璃钢/复合材料,1998(1):24-27. |
| [10] | 翁永华,马满珍,虞叶琴.GF/PET混纤纱复合材料成型工艺条件与材料性能关系的探讨[J].玻璃钢/复合材料,1999(1):12-15. |
| [11] | 丁辛,吴学东.热塑性树脂与连续纤维预混料(包缠纱)的制备技术[J].玻璃钢/复合材料,1997(5):25-27. |
| [12] | 王荣国,刘文博,张东兴,等.连续玻璃纤维增强热塑性复合材料工艺及力学性能的研究[J].航空材料学报,2001,21(2): 44-47. |
| [13] | Hamada H, Maekawa Z, Ikegawa N, et al. Influence of the impregnating property on mechanical properties of commingled yarn composites [J]. Polymer Composites, 1993,14(4): 308-313. |
| [14] | 孙宏杰,张晓明,宋中健.纤维增强热塑性复合材料的预浸渍技术发展概况[J].玻璃钢/复合材料,1999(4):40-44. |
| [15] | Bernhardsson J, Shishoo R. Effect of processing parameters on consolidation quality of GF/PP commingled yarn based composites [ J ]. Journal of Thermoplastic Composite Materials, 2000, 13(7): 292-313. |
| [16] | 李龙,王善元,连续纤维增强热塑性复合材料预浸料的加工方法[J].纤维复合材料,1996(1):21-22. |
| [17] | Wakeman M D, Cain T A, Rudd C D, et al. Compression moulding of glass and polypropylene composites for optimized macro-and micro-mechanical properties-1 commingled glass and polypropylene [J]. Composite Science and Technology,1998, 58(13): 1879-1896. |
| [18] | 李龙,王善元,俞建勇.热压参数对玻璃纤维/聚丙烯喷气混纤纱复合材料性能影响[J].玻璃钢/复合材料,1998(1):20; 21; 27. |
| [19] | Vendramini J, Bas C, Merle G, et al. Commingled poly ( butylenes terephthalate ) /unidirectional glass fiber composites: Influence of the process conditions on the microstructure of poly (butylenes terephthalate)[J]. Polymer Composites, 2000, 21(5): 724-733. |
| [20] | Lauke B, Bunzel U, Schneider K. Effect of hybrid yarn structure on the delamination behaviour of thermoplastic composites [J]. Composites Part A, 1998, 29(9): 1397-1409. |
| [21] | 丁权.Twintex复合纤维--一种新颖的玻纤材料[J].玻璃纤维,1998(4):36-3922. |
| [22] | 吴学东,丁辛.摩擦纺包缠纱纺织预型件及其复合材料的加工[J].玻璃钢/复合材料,1997(6):31-33. |
| [23] | 李龙,王善元,俞建勇.空隙率对喷气混纤纱复合材料力学性能的影响[J].复合材料学报,1999,16(4):68-71. |
| [24] | Czigany T, Ostgathe M, Karger-Kocsis J. Damage development in GF/PET composite sheets with different fabric architecture produced of a commingled yarn [J]. Journal of Reinforced Plastics and Composites, 1998, 17(3): 250-267. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%