研究了在热压条件下制备(SiC,TiB2)/B4C复合材料的烧结机理.认为烧结助剂的加入使本体系成为液相烧结,同时粉料的微细颗粒对复合材料的烧结致密也有重要贡献.分析和测量了制取的复合材料的相组成、显微结构和力学性能.结果表明,采用B4C与Si3N4和少量SiC、TiC为原料,Al2O3+Y2O3为烧结助剂,在烧结温度1800～1880℃,压力30 MPa的热压条件下烧结反应生成了SiC、TiB2和少量的BN,制取了(SiC,TiB2)/B4C复合材料.所形成的晶体显微结构为层片状.制得的试样的硬度、抗弯强度和断裂韧性分别可达HRA88.6、540 MPa和5.6 MPa·m1/2.
参考文献
| [1] | Schwetz K A, Vogt G. Process for the production of dense sintered shaped articles of polycrystalline boron carbide by pressureless sintering [P]. US Pat, 4195066. 1980-03-05. |
| [2] | Prochazka S, Dole S L, Hejna C I. Abnormal grain growth and microcracking in boron carbide [J]. J Am Cream Soc,1985, 68(9): 235-236. |
| [3] | 尹邦跃,王零森,方寅初.纯B4C和掺碳B4C的烧结机制[J].硅酸盐学报,2001,29(1):68-71. |
| [4] | 江东亮.精细陶瓷材料[M].北京:中国物资出版社,2000.158-175. |
| [5] | 邓建新,周军.B4C(W,Ti)C陶瓷复合材料的制备及其性能[J].硅酸盐通报,2002,30(1):16-20. |
| [6] | Suzuya Y, Kiyoshi H. Mechanical and electrical properties of B4C-CrB2 ceramics fabricated by liquid phase sintering [J].Ceramics International, 2003, 29 (3): 299- 304. |
| [7] | 丁硕,温广武,雷廷权,等.由聚碳硅烷生成纳米SiC颗粒增强B4C基复合陶瓷的结构与性能[J].无机材料学报,2002,17(5):1013-1018. |
| [8] | 唐军,谭寿洪,陈忠明.原位生成TiB2颗粒增韧B4C陶瓷的研究[J].粉末冶金技术,1996,14(3):168-174. |
| [9] | Dmitri B, Surya R K. Microstructural evolution during transient plastic phase processing of titanium carbide-titanium boride composites [J]. J Am Ceram Soc, 1996, 79 (7): 1945-1952. |
| [10] | 张宝生,李世波,温广武.添加Al2O3对B4C材料热压烧结行为的研究[J].哈尔滨建筑大学学报,1999,32(3):72-75. |
| [11] | 陆佩文.无机材料科学基础[M].武汉:武汉工业大学出版社,1996.282-306. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%