为了提高沥青基炭纤维表面活性,采用γ-射线辐照对沥青基炭纤维表面改性.用AFM、XPS研究了γ-射线辐照改性后沥青基炭纤维表面结构的变化,用浸润仪测定了改性前后沥青基炭纤维表面能的变化.研究了γ-射线辐照沥青基炭纤维对炭/炭复合材料力学性能的影响,并用SEM分析了炭/炭复合材料断口形貌.结果表明,γ-射线辐照使炭纤维表面含氧官能团和表面粗糙度增加,提高了沥青基炭纤维的表面能;降低了炭/炭复合材料孔隙率,提高了炭/炭复合材料力学性能.
参考文献
[1] | 宋桂明,周玉,王玉金,雷廷权.固体火箭发动机喉衬材料[J].固体火箭技术,1998,21(2):51-55.Song Guiming,Zhou Yu,Wang Yujin,Lei Tingquan.Throat materials for solid rocket motors[J].Journal of Solid Rocket Technology,1998,21(2):51-55. |
[2] | 易法军,韩杰才,杜善义.混杂碳/碳复合材料超高温力学性能实验研究[J].复合材料学报,2003,20(2):118-122.Yi Fajun,Han Jiecai,Du Shanyi.Experimental investigation on mechanical properties of hybrid carbon-carbon composites at ultra-high temperature[J].Acta Materiae Compositae Sinica,2003,20(2):118-122. |
[3] | Oskar Paris,Dieter Loidl,Herwig Peterlik.Texture of PANand pitch-based carbon fibers[J].Carbon,2002,40:551-555. |
[4] | Fumitaka Watanabe,Sumihito Ishida,Yozo Korai,Isao Mochida,Isao Kato,Yukio Sakai,Makoto Kamatsu.Pitchbased carbon fiber of high compressive strength prepared from synthetic isotropic pitch containing mesophase spheres[J].Carbon,1999,37:961-967. |
[5] | Park Soo-Jin,Seo Min-Kang,Lee Young-Seak.Surface characteristics of fluorine-modified PAN-based carbon fibers[J].Carbon,2003,41:723-730. |
[6] | 曹海琳,黄玉东,张志谦.NH4HCO3溶液中PAN-基碳纤维电化学改性机理[J].复合材料学报,2004,21(3):22-27.Cao Hailin,Huang Yudong,Zhang Zhiqian.Mechanisms of surface modification of PAN-based carbon fibers by electrochemical treatment in aqueous ammonium bicarbonate[J].Acta Materiae Compositae Sinica,2004,21(3):22-27. |
[7] | 王成忠,杨小平,于运花,刘承坤.XPS,AFM研究沥青基碳纤维电化学表面处理过程的机制[J].复合材料学报,2002,19(5):28-32.Wang Chengzhong,Yang Xiaoping,Yu Yunhua,Ryu Seungkon.Study on the mechanism of electrochemical oxidized pitch-based carbon fiber by XPS and AFM[J].Acta Materiae CompositaeSinica,2002,19(5):28-32. |
[8] | 贾玲,周丽绘,薛志云,齐会民,胡福增.碳纤维表面等离子接枝及对碳纤维/PAA复合材料ILSS的影响[J].复合材料学报,2004,21(4):45-49.Jia Ling,Zhou Lihui,Xue Zhiyun,Qi Huimin,Hu Fuzeng.Surface of carbon fiber grafted by plasma technology and its influence on the C/PAA composite[J].Acta Materiae Compositae Sinica,2004,21(4):45-49. |
[9] | Leea W H,Leea J G,Reucroftb P J.XPS study of carbon fiber surfaces treated by thermal oxidation in a gas mixture of O2/(O2+N2)[J].Applied Surface Science,2001,171:136-142. |
[10] | Park Soo-Jin,Jang Yu-Sin.X-ray diffraction and X-ray photoelectron spectroscopy studies of Ni-P deposited onto carbon fiber surfaces:Impact properties of a carbon-fiber-reinforced matrix[J].Journal of Colloid and Interface Science,2003,263:170-176. |
[11] | Vijay Kumar Kaushik.Surface characterization of KMnO4 treated carbon fiber precursors using X-ray photoelectron spectroscopy[J].Polymer Testing,2000,19:17-25. |
[12] | Kvon R I,Iinich G N,Chuvilin A L,Likholobov V A.XPS and TEM study of new carbon material:N-containing catalytic filamentous carbon[J].Journal of Molecular Catalysis A:Chemical,2000,158:413-416. |
[13] | 孙乐民,李贺军,张守阳.沥青基炭/炭复合材料的弯曲断裂特征[J].新型炭材料,2001,16(3):28-31.Sun Lemin,Li Hejun,Zhang Shouyang.Fracture characteristics of pitch-based carbon-carbon composites[J].New Carbon Materials,2001,16(3):28-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%