为解决碳纳米管在铜基体中的分散与结合两个问题,运用超声振荡辅助复合电镀制备铜基碳纳米管(Cu/CNTs)复合镀层.利用场发射扫描电镜进行观察,复合镀层微观表面平整,碳纳米管在基体中均匀分散,其与基体结合良好.依据实验结果对超声振荡在复合电镀过程中发挥作用的机制给出了初步的解释.
参考文献
| [1] | Iijima S.Helical microtubes of graphitic carbon[J].Nature,1991,354(6348):56-58. |
| [2] | Hayashida T,Pan L,Nakayama Y.Mechanical and electrical properties of carbon tubule nanocoils[J].Physica B,2002,323(4):352-353. |
| [3] | Phaedon A.Carbon nanotube electronics[J].Chemical Physics,2002,281(3):429-445. |
| [4] | Lau K T,Hui D.Effectiveness of using carbon nanotubes as nano-reinforcements for advanced composite structures[J].Carbon,2002,40(9):1605-1606. |
| [5] | 胡文平,刘云圻,曾鹏举.纳米碳管[J].化学通报,2000,63(2):2-6.Hu Wenping,Liu Yunqin,Zeng Pengju.Carbon nanotube[J].Chemistry,2000,63(2):2-6. |
| [6] | 陈卫祥,涂江平,徐铸德.碳纳米管的特性及其高性能的复合材料[J].复合材料学报,2001,18(4):1-5.Chen Weixiang,Tu Jiangping,Xu Zhude.Characteristics of carbon nanotubes and high-quality composites[J].Acta Materiae Compositae Sinica,2001,18(4):1-5. |
| [7] | 杨邦朝,陈金菊,冯哲圣.碳纳米管的物性及应用[J].电子元件与材料,2003,22(5):44-46.Yang Bangchao,Chen Jinju,Feng Zhesheng.Physical properties and applications of carbon nanotubes[J].Electronic Components and Materials,2003,22(5):44-46. |
| [8] | Ajayan P M,Stephan O,Coliex C,et al.Aligned carbon nanotube arrays formed by cutting a polymer resin nanotube composite[J].Science,1994,265(16):1212-1214. |
| [9] | Dujardin E,Ebbesen T W,Hiura H.Capillarity and wetting of carbon nanotubes[J].Science,1994,265(18):1850-1851. |
| [10] | 王杨勇,井新利,强军锋.聚苯胺/碳纳米管的原位复合[J].复合材料学报,2004,21(3):38-43.Wang Yangyong,Jing Xinli,Qiang Junfeng.In-situ polymerization of polyaniline/carbon nanotube composite[J].Acta Materiae Compositae Sinica,2004,21(3):38-43. |
| [11] | 沈曾民,杨子芹,赵东林,等.碳纳米管/ABS树脂基复合材料的力学性能和雷达波吸收性能的研究[J].复合材料学报,2003,20(2):25-29.Shen Zengmin,Yang Ziqin,Zhao Donglin,et al.Mechanical properties and the radar absorbing property of carbon nanotubes reinforced ABS composite[J].Acta Materiae Compositae Sinica,2003,20(2):25-29. |
| [12] | 沈金龙,李四年,余天庆,等.粉末冶金法制备镁基复合材料的力学性能和增强机理研究[J].铸造技术,2005,26(4):309-312.Shen Jinlong,Li Sinian,Yu Tianqing,et al.Study on the mechanical properties and strengthening mechanism of magnesium matrix composite by powder metallurgy[J].Foundry Technology,2005,26(4):309-312. |
| [13] | 凤仪,袁海龙,张敏.碳纳米管-银复合材料的制备工艺和电导率[J].中国有色金属学报,2004,14(9):1451-1455.Feng Yi,Yuan Hailong,Zhang Min.Processing and electrical conductivity of carbon nanotubes-silver composites[J].The Chinese Journal of Nonferrous Metals,2004,14(9):1451-1455. |
| [14] | 凤仪,袁海龙,张敏,等.碳纳米管银复合材料力学性能研究[J].材料热处理学报,2005,26(2):23-27.Feng Yi,Yuan Hailong,Zhang Min,et al.Processing and mechanical properties of carbon nanotubes-silver composites[J].Transactions of Materials and Heat Treatment,2005,26(2):23-27. |
| [15] | 袁海龙,凤仪.碳纳米管的化学镀铜[J].中国有色金属学报,2004,14(4):666-669.Yuan Hailong,Feng Yi.Electroless plating of carbon nanotube with copper[J].The Chinese Journal of Nonferrous Metals,2004,14(4):666-669. |
| [16] | 陈小华,王健雄,邓福铭,等.碳纳米管的化学镀镍研究[J].新型炭材料,2000,15(4):39-43.Chen Xiaohua,Wang Jianxiong,Deng Fuming,et al.Electroless plating of carbon nanotube with nickel[J].New Carbon Materials,2000,15(4):39-43. |
| [17] | 吴元康,余焜,熊晓辉,等.纳米晶金刚石织构粒子增强银基电接触复合镀层的研究[J].电镀与涂饰,2002,21(3):6-11.Wu Yuankang,Yu Kun,Xiong Xiaohui,et al.Studies on electric contact silver based composite deposit intensified with nano crystal diamond particles[J].Electroplating and Finishing,2002,21(3):6-11. |
| [18] | Arai S,Endo M,Kaneko N.Ni-deposited multi-walled carbon nanotubes by electrodeposition[J].Carbon,2004,42(3):641-644. |
| [19] | Arai S,Endo M.Carbon nanofiber-copper composites fabricated by electroplating[J].Electrochemical and Solid-State Letter,2004,7(3):25-26. |
| [20] | Celis J P,Roos J R,Buelens C.A mathematical model for the electrolytic codeposition of particles with a metallic matrix[J].J Electrochem Soc,1987,134(6):1402-1408. |
| [21] | Flahaut E,Peigney A,Laurent Ch,et al.Carbon nanotubemetal-oxide nanocomposites:Microstructure electrical conductivity and mechanical properties[J].Acta Materialia,2000,48(14):3803-3812. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%